BASF Nypel® 2367G HS BK 15/25% Glass/Mineral Filled PA6 (Dry)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer BASF
Trade Name Nypel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Nypel® 2367G HS BK 15/25% Glass/Mineral Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nypel 2367G HS BK-4 is a black pigmented, heat stabilized, 40% mineral and glass fiber reinforced injection molding compound based on recycled PA6 feedstocks. It possesses a balance of engineering properties in combination with excellent dimensional stability, low warp and good resistance to sink-mark formation. It is available in natural and black.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ISO 1183
Water Absorption 0.90 %
0.90 %
24 hour; ISO Test
5.7 %
5.7 %
ISO 62
Moisture Absorption at Equilibrium 1.6 %
1.6 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM Test
Tensile Strength at Break 120 MPa
17400 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 120 MPa
17400 psi
5mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
3.0 %
3.0 %
0.2 in/min; ASTM Test
Flexural Strength 170 MPa
24700 psi
ISO Data
Flexural Modulus 6.63 GPa
962 ksi
ISO Data
7.59 GPa
1100 ksi
ASTM Test
Izod Impact, Notched 0.500 J/cm

@Thickness 3.17 mm
0.937 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO Test
Charpy Impact Unnotched 4.80 J/cm²
22.8 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.450 J/cm²
2.14 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 31.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
17.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 217 °C
423 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 198 °C
388 °F
ISO 75
203 °C
397 °F
ASTM Test
Descriptive Properties Value Comments
Color BK
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding