BASF Petra® 7030 GY6128 30% Glass Filled PET
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced |
| Manufacturer | BASF |
| Trade Name | Petra® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Petra® 7030 GY6128 30% Glass Filled PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Petra 7030 GY6128 is a grey pigmented, high flow 30% glass fiber reinforced injection molding compound based on post-consumer and post-industrial recycled polyethylene terephthalate feedstock. It offers strength, stiffness, and rigidity combined with excellent dimensional stability, creep resistance and high temperature performance. It's improved flow results in excellent urface aesthetics which can eliminate the need for painting parts.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Viscosity Measurement | 0.55 | 0.55 | Inherent Viscosity |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM Test |
| Tensile Strength at Break | 150 MPa | 21800 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 |
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |
| Flexural Strength | 240 MPa | 34800 psi | ASTM Test |
| Flexural Modulus | 8.83 GPa | 1280 ksi | ISO Data |
| 9.09 GPa | 1320 ksi | ASTM Test | |
| Izod Impact, Notched | 1.00 J/cm @Thickness 3.17 mm |
1.87 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Izod Impact, Notched (ISO) | 9.50 kJ/m² | 4.52 ft-lb/in² | ISO Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
12.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM Test |
| Melting Point | 245 °C | 473 °F | 10 K/min |
| 245 °C | 473 °F | ASTM Test | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 275 °C | 527 °F | Injection molding |
| Mold Temperature | 115 °C | 239 °F | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | GY6128 | |
| Commercial Status | Active America | |
| Form | Pellets | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| UL.UL-C | Yes |