BASF Styrodur® 3035 CS Extruded Rigid Polystyrene Foam (Europe)

Category Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS) , Polystyrene, Extrusion Grade
Manufacturer BASF
Trade Name Styrodur®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Styrodur® 3035 CS Extruded Rigid Polystyrene Foam (Europe).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Styrodur C is the green extruded rigid polystyrene foam (XPS) from BASF. As a thermal insulation, it makes a significant contribution to climate protection by reducing CO2 emissions. The key features of Styrodur C are high compressive strength, low water absorption, and outstanding thermal insulation. It is also rot-proof and easy to handle on site. Compressive strength is the major factor that differentiates the various grades of Styrodur C.Applications: Load-bearing floor slabs, Domestic floors, Load-bearing floors, Perimeter floor slabs, Perimeter basement walls, Perimeter subsoil water areas, Cavity walls, Pitched roofs, Ceilings, and WarehousesInformation provided by BASF
Physical Properties Metric English Comments
Density 0.0330 g/cc
0.00119 lb/in³
Water Absorption 0.20 %
0.20 %
by immersion; DIN EN 12087
<= 3.0 %
<= 3.0 %
by diffusion; DIN EN 12088
Water Vapor Transmission 50.0 - 150 g/m²/day
3.22 - 9.66 g/100 in²/day
DIN EN 12086
Deformation <= 5.0 %

@Pressure 0.0400 MPa,
Temperature 70.0 °C
<= 5.0 %

@Pressure 5.80 psi,
Temperature 158 °F
DIN EN 1605
Mechanical Properties Metric English Comments
Tensile Strength 0.300 MPa
43.5 psi
Creep Strength 0.130 MPa

@Strain <=2.00 %
18.9 psi

@Strain <=2.00 %
Compressive; DIN EN 1606
0.130 MPa

@Strain <=2.00 %
18.9 psi

@Strain <=2.00 %
Compressive; long-term; 50 years; DIN EN 1606
0.160 MPa

@Strain <=2.00 %,
Time 3.60e+6 sec
23.2 psi

@Strain <=2.00 %,
Time 1000 hour
Compressive; mid-term; DIN EN 1606
Modulus of Elasticity 0.00650 GPa
0.943 ksi
Long-term; DIN EN 826
0.0200 GPa
2.90 ksi
DIN EN 826
Tensile Modulus 0.0200 GPa
2.90 ksi
Flexural Strength 0.500 MPa
72.5 psi
Compressive Strength 0.130 MPa
18.9 psi
s<sub>perm</sub>; DIBT Z-23.34-13525
0.180 MPa
26.1 psi
f<sub>cd</sub>; DIBT Z-23.34-13525
0.300 MPa

@Strain 10.0 %
43.5 psi

@Strain 10.0 %
DIN EN 826
Compressive Modulus 0.00500 GPa
0.725 ksi
Elasticity; Long term E50; DIN EN 826
0.0200 GPa
2.90 ksi
Elasticity; Short term E; DIN EN 826
Shear Strength 0.300 MPa
43.5 psi
0.300 MPa
43.5 psi
Allowable
Adhesive Bond Strength <= 0.100 MPa
<= 14.5 psi
on concrete
<= 0.100 MPa
<= 14.5 psi
on mineralic surfaces
<= 0.100 MPa
<= 14.5 psi
on gluing mortar
<= 0.100 MPa
<= 14.5 psi
on plasters
>= 0.200 MPa
>= 29.0 psi
on metals
>= 0.200 MPa
>= 29.0 psi
on wood
>= 0.200 MPa
>= 29.0 psi
on plastic
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 8.00 µm/m-°C
4.44 µin/in-°F
DIN 53752
CTE, linear, Transverse to Flow 6.00 µm/m-°C
3.33 µin/in-°F
DIN 53752
Thermal Conductivity 0.0330 W/m-K
0.229 BTU-in/hr-ft²-°F
Moisture Content: 0%
0.0340 W/m-K
0.236 BTU-in/hr-ft²-°F
Moisture Content: 1%
0.0340 W/m-K
0.236 BTU-in/hr-ft²-°F
Moisture Content: 2%
0.0350 W/m-K
0.243 BTU-in/hr-ft²-°F
Moisture Content: 3%
0.0350 W/m-K
0.243 BTU-in/hr-ft²-°F
Moisture Content: 4%
0.0360 W/m-K
0.250 BTU-in/hr-ft²-°F
Moisture Content: 5%
0.0370 W/m-K
0.257 BTU-in/hr-ft²-°F
Moisture Content: 6%
0.0380 W/m-K
0.264 BTU-in/hr-ft²-°F
Moisture Content: 8%
0.0390 W/m-K
0.271 BTU-in/hr-ft²-°F
Moisture Content: 10%
0.0400 W/m-K
0.278 BTU-in/hr-ft²-°F
Moisture Content: 12%
0.0240 W/m-K

@Temperature -80.0 °C
0.167 BTU-in/hr-ft²-°F

@Temperature -112 °F
0.0260 W/m-K

@Temperature -60.0 °C
0.180 BTU-in/hr-ft²-°F

@Temperature -76.0 °F
0.0280 W/m-K

@Temperature -40.0 °C
0.194 BTU-in/hr-ft²-°F

@Temperature -40.0 °F
0.0300 W/m-K

@Temperature -20.0 °C
0.208 BTU-in/hr-ft²-°F

@Temperature -4.00 °F
0.0320 W/m-K

@Temperature 0.000 °C
0.222 BTU-in/hr-ft²-°F

@Temperature 32.0 °F
0.0330 W/m-K

@Temperature 10.0 °C
0.229 BTU-in/hr-ft²-°F

@Temperature 50.0 °F
0.0340 W/m-K

@Temperature 20.0 °C
0.236 BTU-in/hr-ft²-°F

@Temperature 68.0 °F
0.0350 W/m-K

@Temperature 30.0 °C
0.243 BTU-in/hr-ft²-°F

@Temperature 86.0 °F
0.0360 W/m-K

@Temperature 40.0 °C
0.250 BTU-in/hr-ft²-°F

@Temperature 104 °F
0.0370 W/m-K

@Temperature 50.0 °C
0.257 BTU-in/hr-ft²-°F

@Temperature 122 °F
0.0310 W/m-K

@Thickness 30.0 mm
0.215 BTU-in/hr-ft²-°F

@Thickness 1.18 in
DIN EN 13164
0.0320 W/m-K

@Thickness 40.0 mm
0.222 BTU-in/hr-ft²-°F

@Thickness 1.57 in
DIN EN 13164
0.0330 W/m-K

@Thickness 50.0 mm
0.229 BTU-in/hr-ft²-°F

@Thickness 1.97 in
DIN EN 13164
0.0340 W/m-K

@Thickness 60.0 mm
0.236 BTU-in/hr-ft²-°F

@Thickness 2.36 in
DIN EN 13164
0.0350 W/m-K

@Thickness 80.0 mm
0.243 BTU-in/hr-ft²-°F

@Thickness 3.15 in
DIN EN 13164
0.0370 W/m-K

@Thickness 100 mm
0.257 BTU-in/hr-ft²-°F

@Thickness 3.94 in
DIN EN 13164
0.0380 W/m-K

@Thickness 120 mm
0.264 BTU-in/hr-ft²-°F

@Thickness 4.72 in
DIN EN 13164
0.0380 W/m-K

@Thickness 140 mm
0.264 BTU-in/hr-ft²-°F

@Thickness 5.51 in
DIN EN 13164
0.0380 W/m-K

@Thickness 160 mm
0.264 BTU-in/hr-ft²-°F

@Thickness 6.30 in
DIN EN 13164
0.0400 W/m-K

@Thickness 180 mm
0.278 BTU-in/hr-ft²-°F

@Thickness 7.09 in
DIN EN 13164
Maximum Service Temperature, Air 75.0 °C
167 °F
DIN EN 14706
Descriptive Properties Value Comments
Commercial Status Europe
Dimensional Stability at Heat < 5%
70°C, 90% rh; DIN EN 1604
Dynamic Stiffness 120-800 MN/m3
130 MN/mm2
120 mm
150 MN/mm2
100 mm
190 MN/mm2
80 mm
260 MN/mm2
60 mm
390 MN/mm2
40 mm
780 MN/mm2
20 mm
Freeze-Thaw-Resistance <1%
DIN EN1209
Long-term Bedding Modulus for 30-160 mm 0.036 - 0.217 N/mm3
EN 1606