BASF Ultradur S 4090 G6 30% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultradur S
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur S 4090 G6 30% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultradur S 4090 G6 is a 30% glass reinforced PBT+ASA blend. It produces moldings with good surface finish, is resistant to chemicals and stress cracking, and has low shrinkage and warpage.Applications: Plug connectors, housings and sunroof.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
DIN 53495/1L
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.
Viscosity Test 105 cm³/g
105 cm³/g
Viscosity number; ISO 1628
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Sheet
0.0029 cm/cm
0.0029 in/in
60x60x2mm; ISO 294
Linear Mold Shrinkage, Transverse 0.0075 cm/cm
0.0075 in/in
60x60x2mm; ISO 294
0.0075 cm/cm
0.0075 in/in
Sheet
Melt Flow 23.9 g/10 min

@Load 2.16 kg,
Temperature 275 °C
23.9 g/10 min

@Load 4.76 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 164 MPa
23800 psi
ISO 2039-1
Tensile Strength at Break 125 MPa
18100 psi
5mm/min; ISO 527-2
Tensile Strength 65.0 MPa

@Temperature 100 °C
9430 psi

@Temperature 212 °F
ISO 527
120 MPa

@Temperature 50.0 °C
17400 psi

@Temperature 122 °F
ISO 527
150 MPa

@Temperature 23.0 °C
21800 psi

@Temperature 73.4 °F
ISO 527
195 MPa

@Temperature -40.0 °C
28300 psi

@Temperature -40.0 °F
ISO 527
Elongation at Break 2.2 %
2.2 %
5mm/min; ISO 527-2
Modulus of Elasticity 9.70 GPa
1410 ksi
ISO 527-2
Flexural Strength 183 MPa
26500 psi
ISO 178
Charpy Impact Unnotched 5.90 J/cm²
28.1 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
Dart Drop, Total Energy <= 5.00 J
<= 3.69 ft-lb
ISO 6603-1
Tensile Creep Modulus, 1000 hours 6700 MPa
972000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 3.00 µm/m-°C

@Temperature 23.0 - 80.0 °C
1.67 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 53752
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
IEC 1006
Thermal Conductivity 0.290 W/m-K
2.01 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 - 225 °C
428 - 437 °F
Maximum Service Temperature, Air 110 °C
230 °F
at 50% loss of tensile strength after 20000h; IEC 216-1
140 °C
284 °F
at 50% loss of tensile strength after 5000h; IEC 216-1
170 °C
338 °F
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
ISO 75-2
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Flame Spread <= 100 mm/min
<= 3.94 in/min
DIN 75200
Glow Wire Test 760 °C

@Thickness 3.00 mm
1400 °F

@Thickness 0.118 in
IEC 695
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+15 ohm-cm
3.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
3.7

@Frequency 1.00e+6 Hz
IEC 60250
3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
IEC 60250
Dielectric Strength 95.0 kV/mm
2410 kV/in
IEC 243/1
Dissipation Factor 0.0030

@Frequency 100 Hz
0.0030

@Frequency 100 Hz
IEC 60250
0.018

@Frequency 1.00e+6 Hz
0.018

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 125 V
125 V
Test solution B; IEC 60112
500 V
500 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 275 °C
482 - 527 °F
Injection molding
270 °C
518 °F
for shrinkage test
Mold Temperature 60.0 - 100 °C
140 - 212 °F
80.0 °C
176 °F
for shrinkage test
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
Light stabilized or stable to light
Lubricant
U.V. stabilized or stable to weather