BASF Ultradur® S 4090 G6X 30% Glass Filled PBT
| Category | Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced |
| Manufacturer | BASF |
| Trade Name | Ultradur® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur® S 4090 G6X 30% Glass Filled PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Is a PBT + ASA, low-warpage, free-flowing injection-molding grades with very good processing capabilities, containing 30% of glass fibers for industrial parts with high dimensional stability, for example internal components for vehicles, plug connectors and housings.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH |
| Viscosity Measurement | 104 | 104 | [ml/g]; Viscosity number; ISO 1628 |
| 70 @Temperature 290 °C |
70 @Temperature 554 °F |
20 mins plasticating | |
| 75 @Temperature 280 °C |
75 @Temperature 536 °F |
30 mins plasticating | |
| 75 @Temperature 300 °C |
75 @Temperature 572 °F |
10 mins plasticating | |
| 90 @Temperature 270 °C |
90 @Temperature 518 °F |
30 mins plasticating | |
| 95 @Temperature 290 °C |
95 @Temperature 554 °F |
10 mins plasticating | |
| 100 @Temperature 300 °C |
100 @Temperature 572 °F |
5 mins plasticating | |
| 100 @Temperature 260 °C |
100 @Temperature 500 °F |
30 mins plasticating | |
| 105 @Temperature 280 °C |
105 @Temperature 536 °F |
10 mins plasticating | |
| 106 @Temperature 250 °C |
106 @Temperature 482 °F |
30 mins plasticating | |
| 110 @Temperature 270 °C |
110 @Temperature 518 °F |
10 mins plasticating | |
| 115 @Temperature 260 °C |
115 @Temperature 500 °F |
10 mins plasticating | |
| 115 @Temperature 240 °C |
115 @Temperature 464 °F |
30 mins plasticating | |
| 117 @Temperature 250 °C |
117 @Temperature 482 °F |
10 mins plasticating | |
| 120 @Temperature 240 °C |
120 @Temperature 464 °F |
10 mins plasticating | |
| Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | Sheet |
| 0.0029 cm/cm | 0.0029 in/in | 60x60x2 mm; ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0082 cm/cm | 0.0082 in/in | 60x60x2 mm; ISO 294 |
| 0.0095 cm/cm | 0.0095 in/in | Sheet | |
| Melt Flow | 29.4 g/10 min @Load 2.16 kg, Temperature 275 °C |
29.4 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 132 MPa | 19100 psi | 50 mm/min; ISO 527-2 |
| Elongation at Yield | 2.5 % | 2.5 % | 50 mm/min; ISO 527-2 |
| Modulus of Elasticity | 9.80 GPa | 1420 ksi | ISO 527-2 |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.40 J/cm² @Temperature 23.0 °C |
30.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | 23; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
16.7 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 |
| Maximum Service Temperature, Air | 170 °C | 338 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Diameter 0.800 mm |
HB @Diameter 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.50e+15 ohm-cm | 1.50e+15 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 93 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 250 |
| 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 250 | |
| Dielectric Strength | 41.0 kV/mm | 1040 kV/in | IEC 243/1 |
| Dissipation Factor | 0.0046 @Frequency 100 Hz |
0.0046 @Frequency 100 Hz |
IEC 250 |
| 0.0202 @Frequency 1.00e+6 Hz |
0.0202 @Frequency 1.00e+6 Hz |
IEC 250 | |
| Comparative Tracking Index | 425 V | 425 V | Test solution A; IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat |
| Zone 1 | 260 °C | 500 °F | Feeding zone |
| Zone 2 | 265 °C | 509 °F | Compression |
| Zone 3 | 270 °C | 518 °F | Metering-zone |
| Zone 4 | 270 °C | 518 °F | Nozzle |
| Melt Temperature | >= 260 °C | >= 500 °F | Injection-molding |
| 270 °C | 518 °F | for shrinkage test, Optimal | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| 80.0 °C | 176 °F | for shrinkage test, Optimal | |
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural and Black | |
| Commercial Status | Europe | |
| Peripheral screw speed | < 0.25 m/s | |
| Primary Processing Technique | Injection Molding |