BASF Ultraform N 2310P Q600 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer BASF
Trade Name Ultraform N
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultraform N 2310P Q600 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultraform N2310P Q600 is a general-purpose injection molding POM grade containing special lubricant. Low frictional coefficient giving extremely low wear with otherwise unaltered mechanical properties.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Melt Flow 7.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 145 MPa
21000 psi
IEC 2039
Tensile Strength, Yield 61.0 MPa
8850 psi
50mm/min; ISO 527
Elongation at Break 31 %
31 %
ISO 527
Elongation at Yield 9.3 %
9.3 %
ISO 527
Modulus of Elasticity 2.60 GPa
377 ksi
SIO 527
Izod Impact, Notched 0.550 J/cm

@Temperature -30.0 °C
1.03 ft-lb/in

@Temperature -22.0 °F
ISO 180/A
0.530 J/cm

@Thickness 584 mm
0.993 ft-lb/in

@Thickness 23.0 in
ISO 180/A
Charpy Impact Unnotched 20.0 J/cm²
95.2 ft-lb/in²
ISO 179
18.0 J/cm²

@Temperature -30.0 °C
85.7 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Tensile Creep Modulus, 1000 hours 1300 MPa
189000 psi
ISO 899
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 11.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
6.11 µin/in-°F

@Temperature 73.4 - 131 °F
DIN 53752
Melting Point 166 °C
331 °F
DIN 53765
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
ISO 75
Vicat Softening Point 150 °C
302 °F
(50 °C/h / 50N) - B/50; ISO 306
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Constant 3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
IEC 60250
3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 60243-1
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
IEC 60250
0.0050

@Frequency 1.00e+6 Hz
0.0050

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test Solution A; IEC 60112
600 V
600 V
Test Solution B; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 190 - 230 °C
374 - 446 °F
Mold Temperature 60.0 - 120 °C
140 - 248 °F
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding