BASF Ultraform® N2650 Z4 (LEV) POM

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	BASF
Trade Name	Ultraform®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultraform® N2650 Z4 (LEV) POM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Is a POM + PUR, elastomer-modified injection-molding grades with high impact strength for clips, snap and fastening elements, also for components subject to impact stress.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.35 g/cc	0.0488 lb/in³	ISO 1183
Water Absorption	0.80 %	0.80 %	Saturation; ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C; 50% RH; ISO 62
Melt Flow	8.1 g/10 min @Load 2.16 kg, Temperature 190 °C	8.1 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	80.0 MPa @Load 36.5 kg, Time 30.0 sec	11600 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
Tensile Strength, Yield	45.0 MPa	6530 psi	50 mm/min; ISO 527-2
Elongation at Break	40 %	40 %	ISO 527-2
Elongation at Yield	16 %	16 %	ISO 527-2
Modulus of Elasticity	1.50 GPa	218 ksi	ISO 527-2
Izod Impact, Notched (ISO)	7.00 kJ/m² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	ISO 180/A
	12.0 kJ/m² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	ISO 180/A
Charpy Impact Unnotched	27.0 J/cm² @Temperature -30.0 °C	128 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.800 J/cm² @Temperature -30.0 °C	3.81 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	1.50 J/cm² @Temperature 23.0 °C	7.14 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	500 MPa	72500 psi	ISO 899-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	13.0 µm/m-°C @Temperature 23.0 - 55.0 °C	7.22 µin/in-°F @Temperature 73.4 - 131 °F	DIN 53752
Melting Point	167 °C	333 °F	DIN 53765
Maximum Service Temperature, Air	100 °C	212 °F
Deflection Temperature at 1.8 MPa (264 psi)	80.0 °C	176 °F	ISO 75-2
Vicat Softening Point	130 °C	266 °F	ISO 306

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 ohm-cm	1.00e+11 ohm-cm	IEC 60093
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm	IEC 60093
Dielectric Constant	4.2 @Frequency 1.00e+6 Hz	4.2 @Frequency 1.00e+6 Hz	IEC 60250
	4.3 @Frequency 100 Hz	4.3 @Frequency 100 Hz	IEC 60250
Dielectric Strength	32.0 kV/mm	813 kV/in	IEC 60243-1
Dissipation Factor	0.012 @Frequency 100 Hz	0.012 @Frequency 100 Hz	IEC 60250
	0.017 @Frequency 1.00e+6 Hz	0.017 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test solution A; IEC 60112
	600 V	600 V	Test solution B; IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	190 - 215 °C	374 - 419 °F	Injection-molding
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F

Descriptive Properties	Value	Comments
Commercial Status	Europe
Primary Processing Technique	Injection Molding