BASF Ultraform® N2650 Z6 POM + PUR
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultraform® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultraform® N2650 Z6 POM + PUR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Elastomer-modified injection molding grade for applications requiring highest impact strength together with low stiffness.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.850 g/cc | 0.0307 lb/in³ | |
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62 |
| Melt Flow | 9.31 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.31 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527-1/-2 |
| Elongation at Break | 44 % | 44 % | 50 mm/min, Nominal; ISO 527-1/-2 |
| Elongation at Yield | 19 % | 19 % | 50 mm/min; ISO 527-1/-2 |
| Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 24.0 J/cm² @Temperature -30.0 °C |
114 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 500 MPa @Strain <=0.500 % |
72500 psi @Strain <=0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C @Temperature 23.0 - 55.0 °C |
77.8 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 |
| Melting Point | 166 °C | 331 °F | ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1/-2 |
| Decomposition Temperature | >= 240 °C | >= 464 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.3 @Frequency 1.00e+6 Hz |
4.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.025 @Frequency 1.00e+6 Hz |
0.025 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | Hopper Throat |
| Zone 1 | 200 °C | 392 °F | Feed zone |
| Zone 2 | 200 °C | 392 °F | Compression |
| Zone 3 | 200 °C | 392 °F | Metering-zone |
| Zone 4 | 200 °C | 392 °F | Nozzle |
| Melt Temperature | 200 °C | 392 °F | Optimal |
| 190 - 215 °C | 374 - 419 °F | Injection molding | |
| Mold Temperature | 60.0 °C | 140 °F | Optimal |
| 60.0 - 80.0 °C | 140 - 176 °F | Injection molding | |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 3 hour | 3 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | 320 - 340 °C | ASTM D1929 |
| Peripheral screw speed | <0.3 m/s |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE Z406 Thermoplastic Elastomer, SEBS-based
- H.C. Starck Amperit® 205.5 Dense Coated Nickel Graphite 75-25 (Ni-C)
- H.C. Starck Amperit® 740.8 Aluminum Oxide (Al2O3)
- SABIC Innovative Plastics LNP LUBRICOMP KI001XXJ Acetal
- Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA), 33% Glass Fiber (Dry)
- Universal Wire Works 6Al-4V (AMS 4954) Titanium Alloy Filler Metal
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR N990 (MT) Filler
- Diamond Polymers Diamaloy ABS VP-22 Flame Retardant ABS
- Axiall 8852 Moldings & Extrusions Flexible PVC
- 3M 2552 Damping Foil
Copyright © lookpolymers.com All Rights Reserved