BASF Ultraform® S1320 003 POM

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	BASF
Trade Name	Ultraform®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultraform® S1320 003 POM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Is a POM, free-flowing, rapidly solidifying grade for moldings difficult to produce by injection molding and having low wall thicknesses, higher stiffness and thermal stability.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³	ISO 1183
Water Absorption	0.80 %	0.80 %	Saturation; ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C; 50% RH; ISO 62
Melt Flow	12.9 g/10 min @Load 2.16 kg, Temperature 190 °C	12.9 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	165 MPa @Load 36.5 kg, Time 30.0 sec	23900 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
Tensile Strength, Yield	68.0 MPa	9860 psi	50 mm/min; ISO 527-2
Elongation at Break	25 %	25 %	ISO 527-2
Elongation at Yield	9.0 %	9.0 %	ISO 527-2
Modulus of Elasticity	3.00 GPa	435 ksi	ISO 527-2
Izod Impact, Notched (ISO)	5.00 kJ/m² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 180/A
	5.50 kJ/m² @Temperature 23.0 °C	2.62 ft-lb/in² @Temperature 73.4 °F	ISO 180/A
Charpy Impact Unnotched	17.0 J/cm² @Temperature -30.0 °C	80.9 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	17.0 J/cm² @Temperature 23.0 °C	80.9 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.550 J/cm² @Temperature -30.0 °C	2.62 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.550 J/cm² @Temperature 23.0 °C	2.62 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	1450 MPa	210000 psi	ISO 899-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	11.0 µm/m-°C @Temperature 23.0 - 55.0 °C	6.11 µin/in-°F @Temperature 73.4 - 131 °F	DIN 53752
Melting Point	171 °C	340 °F	DIN 53765
Maximum Service Temperature, Air	100 °C	212 °F
Deflection Temperature at 1.8 MPa (264 psi)	100 °C	212 °F	ISO 75-2
Vicat Softening Point	150 °C	302 °F	ISO 306

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	IEC 60093
Dielectric Constant	3.7 @Frequency 1.00e+6 Hz	3.7 @Frequency 1.00e+6 Hz	IEC 60250
	3.7 @Frequency 100 Hz	3.7 @Frequency 100 Hz	IEC 60250
Dielectric Strength	40.0 kV/mm	1020 kV/in	IEC 60243-1
Dissipation Factor	0.0020 @Frequency 100 Hz	0.0020 @Frequency 100 Hz	IEC 60250
	0.0050 @Frequency 1.00e+6 Hz	0.0050 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test solution A; IEC 60112
	600 V	600 V	Test solution B; IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	190 - 230 °C	374 - 446 °F	Injection-molding
Mold Temperature	60.0 - 120 °C	140 - 248 °F

Descriptive Properties	Value	Comments
Commercial Status	Europe
Primary Processing Technique	Injection Molding