BASF Ultramid® 8253 HS PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8253 HS PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8253 HS is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased flexibility. It is also available in non-heat stabilized (Ultramid 8253) and/or pigmented versions.
Physical Properties Metric English Comments
Water Absorption 1.5 %
1.5 %
24 hour; ISO Test
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature -40.0 °C
10200 psi

@Temperature -40.0 °F
ISO Data
70.0 MPa

@Temperature -40.0 °C
10200 psi

@Temperature -40.0 °F
ASTM Test
Tensile Strength, Yield 32.0 MPa
4640 psi
2 in/min; ASTM Test
20.0 MPa

@Temperature 80.0 °C
2900 psi

@Temperature 176 °F
ASTM Test
20.0 MPa

@Temperature 80.0 °C
2900 psi

@Temperature 176 °F
ISO Data
116 MPa

@Temperature -40.0 °C
16800 psi

@Temperature -40.0 °F
ASTM Test
116 MPa

@Temperature -40.0 °C
16800 psi

@Temperature -40.0 °F
ISO Data
Elongation at Break >= 100 %
>= 100 %
2 in/min; ASTM Test
20 %

@Temperature -40.0 °C
20 %

@Temperature -40.0 °F
ASTM Test
20 %

@Temperature -40.0 °C
20 %

@Temperature -40.0 °F
ISO Data
Elongation at Yield 15 %
15 %
2 in/min; ASTM Test
30 %

@Temperature 120 °C
30 %

@Temperature 248 °F
ASTM Test
30 %

@Temperature 80.0 °C
30 %

@Temperature 176 °F
ISO Data
Tensile Modulus 0.220 GPa

@Temperature 120 °C
31.9 ksi

@Temperature 248 °F
ISO Data
0.370 GPa

@Temperature 80.0 °C
53.7 ksi

@Temperature 176 °F
ISO Data
3.30 GPa

@Temperature -40.0 °C
479 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 32.0 MPa
4640 psi
ASTM Test
141 MPa

@Temperature -40.0 °C
20500 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 0.670 GPa
97.2 ksi
ASTM Test
Izod Impact, Notched 0.640 J/cm

@Temperature -40.0 °C
1.20 ft-lb/in

@Temperature -40.0 °F
ASTM Test
NB

@Thickness 3.17 mm
NB

@Thickness 0.125 in
ASTM Test
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ASTM Test
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Impact Modified Yes
Primary Processing Technique Injection Molding
UL.UL-C Yes