BASF Ultramid® 8350 HS BK-102 PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8350 HS BK-102 PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8350 HS BK-102 is a type 6, black pigmented, impact modified graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate level of flexibility.

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/in³	ISO 1183
Water Absorption	1.1 %	1.1 %	24 hour; ISO Test
	6.7 %	6.7 %	ISO 62
Moisture Absorption at Equilibrium	1.9 %	1.9 %	23°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.014 cm/cm	0.014 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	78	78	ASTM Test
Tensile Strength, Yield	52.0 MPa	7540 psi	50mm/min; ISO 527
	55.0 MPa	7980 psi	2 in/min; ASTM Test
Elongation at Break	>= 50 %	>= 50 %	50mm/min, Nominal strain; ISO 527
	>= 100 %	>= 100 %	2 in/min; ASTM Test
Elongation at Yield	4.5 %	4.5 %	50mm/min; ISO 527
	5.0 %	5.0 %	2 in/min; ASTM Test
Tensile Modulus	1.80 GPa	261 ksi	1mm/min; ISO 527
Flexural Strength	55.0 MPa	7980 psi	ISO Data
	65.0 MPa	9430 psi	ASTM Test
Flexural Modulus	1.60 GPa	232 ksi	ISO Data
	1.89 GPa	274 ksi	ASTM Test
Izod Impact, Notched	NB @Thickness 3.17 mm	NB @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	NB	NB	ISO Test
	10.0 kJ/m² @Temperature -40.0 °C	4.76 ft-lb/in² @Temperature -40.0 °F	ISO Test
Charpy Impact Unnotched	NB	NB	ISO 179
Charpy Impact, Notched	8.30 J/cm²	39.5 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	106 µm/m-°C @Temperature -30.0 - 30.0 °C	58.9 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	140 °C	284 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F	ISO 75
	56.0 °C	133 °F	ASTM Test
Flammability, UL94	HB	HB
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Comparative Tracking Index	600 V	600 V	IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	280 °C	536 °F	Injection molding
Mold Temperature	70.0 °C	158 °F	Injection molding

Descriptive Properties	Value	Comments
Color	BK-102
Commercial Status	Active America
Form	Pellets
Impact Modified	Yes
Primary Processing Technique	Extrusion
Processing	Injection Molding
	Other Extrusion
	Profile extrusion
Special characteristic	Heat stabilized or stable to heat
UL.UL-C	Yes