BASF Ultramid® A3X4G7 35% Glass Filled PA66 FR (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® A3X4G7 35% Glass Filled PA66 FR (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 35% glass-fiber reinforced injection-molding grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; very high stiffness and strength; outstanding mechanical and electrical properties.Information provided by BASF
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Viscosity Measurement 150
150
ISO 307
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
restricted
Melt Flow 21.9 g/10 min

@Load 5.00 kg,
Temperature 275 °C
21.9 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 130 MPa
18900 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 2.3 %
2.3 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 9.80 GPa
1420 ksi
ISO 527-1/-2
Charpy Impact Unnotched 6.00 J/cm²

@Temperature 23.0 °C
28.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
DIN 53765
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75-1/-2
Flammability, UL94 V-1

@Thickness >=0.400 mm
V-1

@Thickness >=0.0157 in
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe