BASF Ultramid® B35G3 BK 00564 15% Glass Filled PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B35G3 BK 00564 15% Glass Filled PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: 15% glass fiber reinforced injection molding grade e.g. for internal gas pressure applications such as flashing direction switch gears, automobile mirror housings and wheels of mountain bikes.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 7.7 - 8.3 % | 7.7 - 8.3 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.3 - 2.9 % | 2.3 - 2.9 % | ISO 62 |
| 2.6 % | 2.6 % | 50% RH | |
| 8.0 % | 8.0 % | Saturation | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |
| Melt Flow | 55.8 g/10 min | 55.8 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 181 MPa | 26300 psi | ISO 2039-1 |
| Tensile Strength at Break | 126 MPa @Temperature 23.0 °C |
18300 psi @Temperature 73.4 °F |
ISO 527-1/-2 |
| 156 MPa @Temperature -40.0 °C |
22600 psi @Temperature -40.0 °F |
ISO 527-1/-2 | |
| Elongation at Break | 2.9 % | 2.9 % | ISO 527-1/-2 |
| Modulus of Elasticity | 6.10 GPa | 885 ksi | ISO 527-1/-2 |
| Flexural Strength | 189 MPa | 27400 psi | ISO 178 |
| Flexural Modulus | 6.10 GPa | 885 ksi | ISO 527 |
| Charpy Impact Unnotched | 4.70 J/cm² @Temperature 23.0 °C |
22.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.590 J/cm² @Temperature 23.0 °C |
2.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | ISO 75-1/-2 |
| Decomposition Temperature | >= 300 °C | >= 572 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat |
| Zone 1 | 260 °C | 500 °F | Feed Zone |
| Zone 2 | 370 °C | 698 °F | Compression |
| Zone 3 | 280 °C | 536 °F | Metering-zone |
| Zone 4 | 280 °C | 536 °F | Nozzle |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding/Extrusion |
| 280 °C | 536 °F | Optimal | |
| Mold Temperature | 80.0 °C | 176 °F | Optimal |
| 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal |
| <= 0.15 % | <= 0.15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe and North America | |
| Ignition Temperature | >400°C | ASTM D1929 |
| Peripheral screw speed | < 0.3 m/s |