BASF Ultramid® B3UGM210 GR 22866 10/50% Glass/Mineral Filled PA6 FR (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3UGM210 GR 22866 10/50% Glass/Mineral Filled PA6 FR (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Halogen- and phosphorus-free injection-molding grade with very high rigidity, low smoke density and outstanding electrical properties.Information provided by BASF
Physical Properties Metric English Comments
Density 1.67 g/cc
0.0603 lb/in³
ISO 1183
Water Absorption 4.1 - 4.7 %
4.1 - 4.7 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.0 - 1.4 %
1.0 - 1.4 %
23°C; 50% RH; ISO 62
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
restricted
Melt Flow 41.75 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 41.75 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 110 MPa
16000 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 1.8 %
1.8 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 11.0 GPa
1600 ksi
ISO 527-1/-2
Flexural Strength 165 MPa
23900 psi
at max force; ISO 178
Flexural Modulus 10.0 GPa
1450 ksi
ISO 178
Izod Impact, Notched (ISO) 2.50 kJ/m²

@Temperature 23.0 °C
 1.19 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/A
4.50 kJ/m²

@Temperature -30.0 °C
 2.14 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/A
Charpy Impact Unnotched 3.00 J/cm²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
3.00 J/cm²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.250 J/cm²

@Temperature 23.0 °C
 1.19 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 - 60.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 22.2 - 33.3 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 11359-1/-2
CTE, linear, Transverse to Flow 40.0 - 50.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 22.2 - 27.8 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 11359-1/-2
Specific Heat Capacity 1.40 J/g-°C
0.335 BTU/lb-°F
Thermal Conductivity 1.00 W/m-K
6.94 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 149 °C
300 °F
for 50% loss of tensile strength after 20000hr
167 °C
333 °F
for 50% loss of tensile strength after 5000hr
200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ISO 75-1/-2
Flammability, UL94 V-2

@Thickness >=0.750 mm
 V-2

@Thickness >=0.0295 in
V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 4.5

@Frequency 1.00 Hz
 4.5

@Frequency 1.00 Hz
 IEC 60250
Dissipation Factor 0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Descriptive Properties Value Comments
Color GR 22866
Commercial Status Europe