BASF Ultramid® B3WG7 BK00564 35% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3WG7 BK00564 35% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid B3WG7 BK00564 is a 35% glass fiber reinforced, pigmented black, injection molding PA6 grade for highly rigid, dimensionally stable components which are resistant to high temperature aging and have improved retention of properties in a hot water environment.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 188 MPa
27300 psi
5mm/min; ISO 527
Elongation at Break 2.9 %
2.9 %
5mm/min; ISO 527
Tensile Modulus 12.6 GPa
1830 ksi
1mm/min; ISO 527
Flexural Modulus 9.72 GPa
1410 ksi
ISO Data
Izod Impact, Notched (ISO) 11.2 kJ/m²
5.33 ft-lb/in²
ISO Test
Charpy Impact, Notched 0.920 J/cm²
4.38 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75
Descriptive Properties Value Comments
Color BK00564
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding