BASF Ultramid® B3ZG7 OSI BK23273 35% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3ZG7 OSI BK23273 35% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid B3ZG7 OSI BK23273 is a 35% glass reinforced, pigmented black, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet demanding mechanical and chemical requirements for the automotive oil pan application.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Water Absorption 1.1 %
1.1 %
24 hour; ISO Test
Linear Mold Shrinkage, Flow 0.023 cm/cm
0.023 in/in
ISO Data
Linear Mold Shrinkage, Transverse 0.059 cm/cm
0.059 in/in
ISO Data
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 170 MPa
24700 psi
5mm/min; ISO 527
Elongation at Break 3.5 %
3.5 %
5mm/min; ISO 527
Tensile Modulus 10.0 GPa
1450 ksi
1mm/min; ISO 527
Flexural Modulus 8.925 GPa
1294 ksi
ISO Data
Izod Impact, Notched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
ISO Test
17.0 kJ/m²

@Temperature -40.0 °C
8.09 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact Unnotched 10.2 J/cm²
48.5 ft-lb/in²
ISO 179
11.3 J/cm²

@Temperature -30.0 °C
53.8 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 2.60 J/cm²
12.4 ft-lb/in²
ISO 179
1.80 J/cm²

@Temperature -30.0 °C
8.57 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 206 °C
403 °F
ISO 75
Descriptive Properties Value Comments
Color BK23273
Commercial Status Preliminary
Impact Modified Yes
Primary Processing Technique Injection Molding