BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties remain constant after moisture absorption up to a temperature of 60°C [140°F], for instance, for automotive valve housings.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Water Absorption | 4.3 - 5.3 % | 4.3 - 5.3 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 0.80 - 1.2 % | 0.80 - 1.2 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 130 | 130 | ISO 307 |
| Linear Mold Shrinkage | 0.0033 cm/cm | 0.0033 in/in | restricted |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 200 MPa | 29000 psi | 50 mm/min; ISO 527-1/-2 |
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | ISO 527-1/-2 |
| Tensile Creep Modulus, 1000 hours | 8700 MPa @Strain <=0.500 % |
1.26e+6 psi @Strain <=0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 295 °C | 563 °F | DIN 53765 |
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr |
| 160 °C | 320 °F | for 50% loss of tensile strength after 5000hr | |
| 270 °C | 518 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| 1.00e+8 ohm-cm @Temperature 140 °C |
1.00e+8 ohm-cm @Temperature 284 °F |
IEC 60093 | |
| 2.00e+10 ohm-cm @Temperature 100 °C |
2.00e+10 ohm-cm @Temperature 212 °F |
IEC 60093 | |
| 1.00e+11 ohm-cm @Temperature 80.0 °C |
1.00e+11 ohm-cm @Temperature 176 °F |
IEC 60093 | |
| 5.00e+11 ohm-cm @Temperature 60.0 °C |
5.00e+11 ohm-cm @Temperature 140 °F |
IEC 60093 | |
| 1.00e+13 ohm-cm @Temperature 40.0 °C |
1.00e+13 ohm-cm @Temperature 104 °F |
IEC 60093 | |
| 1.00e+15 ohm-cm @Temperature 20.0 °C |
1.00e+15 ohm-cm @Temperature 68.0 °F |
IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.4 @Frequency 1.00 Hz |
4.4 @Frequency 1.00 Hz |
IEC 60250 |
| Dissipation Factor | 0.030 @Frequency 1.00e+6 Hz |
0.030 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe |