BASF Ultramid® KR 4365 G5 35% Glass Filled PA6/6T FR (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® KR 4365 G5 35% Glass Filled PA6/6T FR (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Partially aromatic polyamide; flame retardant based on red phosphorus; low water absorption, high melting point (295°C); low tendency to form deposits on electrical contacts, very resistant to electrolytic corrosion, resistant to soldering temperatures, can be electroplated.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 - 6.0 % | 5.0 - 6.0 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 1.1 - 1.5 % | 1.1 - 1.5 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 130 | 130 | ISO 307 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | restricted |
| Linear Mold Shrinkage, Flow | 0.0041 cm/cm | 0.0041 in/in | TM=320°C, TW=100°C |
| 0.0050 cm/cm | 0.0050 in/in | ISO 2577 | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 140 MPa | 20300 psi | 50 mm/min; ISO 527-1/-2 |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1/-2 |
| Modulus of Elasticity | 8.00 GPa | 1160 ksi | ISO 527-1/-2 |
| Tensile Creep Modulus, 1000 hours | 6400 MPa @Strain <=0.500 % |
928000 psi @Strain <=0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |
| Thermal Conductivity | 0.310 W/m-K | 2.15 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 295 °C | 563 °F | DIN 53765 |
| Maximum Service Temperature, Air | 125 °C | 257 °F | for 50% loss of tensile strength after 20000hr |
| 150 °C | 302 °F | for 50% loss of tensile strength after 5000hr | |
| 270 °C | 518 °F | ||
| Decomposition Temperature | >= 350 °C | >= 662 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat |
| Zone 1 | 300 °C | 572 °F | Feed Zone |
| Zone 2 | 310 °C | 590 °F | Compression |
| Zone 3 | 320 °C | 608 °F | Metering-zone |
| Zone 4 | 320 °C | 608 °F | Nozzle |
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion |
| >= 320 °C | >= 608 °F | Optimal | |
| Mold Temperature | 100 °C | 212 °F | Optimal |
| 80.0 - 120 °C | 176 - 248 °F | Injection-molding | |
| Drying Temperature | 110 °C | 230 °F | |
| Dry Time | 8 hour | 8 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | >470°C | ASTM D1929 |
| Peripheral screw speed | < 0.3 m/s |