BASF Ultramid® S3EG6 Balance 30% Glass Filled PA 610 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® S3EG6 Balance 30% Glass Filled PA 610 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. This means that more than 60 % of the base polymer for the product family consists of sustainable raw materials. Ultramid® S Balance is highly resistant to fuels, oils and greases, to most solvents, aqueous solutions and alkalis. Its resistance to weakly acid media makes it superior to PA 6 and PA 66. Applications: Overmolding metal and electronic components that come into contact with aggressive media, for example wheel speed sensorsHousing and gear components where dimensional stability is a major considerationplug-in connectors, pipes and reservoirs in cooling circuits with high demands on hydrolysis resistanceInformation provided by BASF
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 2.0 - 2.6 %
2.0 - 2.6 %
ISO 62
Moisture Absorption at Equilibrium 0.80 - 1.2 %
0.80 - 1.2 %
ISO 62
Viscosity Measurement 150
150
[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
Test Box 1.5 mm
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
ISO 2577
Melt Flow 39.3 g/10 min

@Load 5.00 kg,
Temperature 275 °C
39.3 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
ISO 527-1/-2
Elongation at Yield 6.0 %
6.0 %
ISO 527-1/-2
Modulus of Elasticity 6.20 GPa
899 ksi
ISO 527-1/-2
Flexural Strength 160 MPa
23200 psi
ISO 178
Flexural Modulus 5.60 GPa
812 ksi
ISO 178
Charpy Impact Unnotched 9.00 J/cm²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.40 J/cm²

@Temperature 23.0 °C
6.66 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ISO 11357-1/-3
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection molding
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection molding/Extrusion
Descriptive Properties Value Comments
Commercial Status Europe