BASF Ultramid® TG3S 15% Glass Filled PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® TG3S 15% Glass Filled PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Ultramid TG3S is a 15% glass reinforced, heat stabilized, impact modified PA6 injection molding compound developed for applications requiring improved toughness in combination with a balance of strength, stiffness, excellent moldability and surface aesthetics.Applications: window hardware, wheel chairs wheels, bicycle wheels, power tool housings, hose clamps, clips and fasteners.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.21 g/cc	0.0437 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
Elongation at Break	3.5 %	3.5 %	ISO 527
Flexural Modulus	4.39 GPa	637 ksi	ISO 178
Izod Impact, Notched (ISO)	5.40 kJ/m² @Temperature -40.0 °C	2.57 ft-lb/in² @Temperature -40.0 °F	ISO 180
	17.0 kJ/m² @Temperature 23.0 °C	8.09 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact, Notched	1.30 J/cm²	6.19 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ISO 3146
Deflection Temperature at 1.8 MPa (264 psi)	180 °C	356 °F	ISO 75
UL RTI, Electrical	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in	746B
UL RTI, Mechanical with Impact	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in	746B
UL RTI, Mechanical without Impact	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in	746B
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Processing Properties	Metric	English	Comments
Zone 1	245 - 275 °C	473 - 527 °F	Rear Zone
Zone 2	260 - 285 °C	500 - 545 °F	Center Zone
Zone 3	270 - 295 °C	518 - 563 °F	Front Zone
Zone 4	270 - 295 °C	518 - 563 °F	Nozzle
Melt Temperature	270 - 295 °C	518 - 563 °F
Mold Temperature	80.0 - 95.0 °C	176 - 203 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	<= 0.080 %	<= 0.080 %

Descriptive Properties	Value	Comments
Commercial Status	North America