BASF Ultrason® E 2010 MR SW 10111 PESU

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer BASF
Trade Name Ultrason®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultrason® E 2010 MR SW 10111 PESU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Unreinforced, medium viscosity standard injection molding grade, demolding optimized. Abbreviated designation according to ISO 1043-1: PESU.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.700 - 0.800 g/cc
0.0253 - 0.0289 lb/in³
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 2.2 %
2.2 %
ISO 62
Moisture Absorption at Equilibrium 0.80 %
0.80 %
23°C; 50% RH; ISO 62
Viscosity Measurement 56
56
[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage, Flow 0.0082 cm/cm
0.0082 in/in
ISO 2577, 294-4
Linear Mold Shrinkage, Transverse 0.0086 cm/cm
0.0086 in/in
ISO 2577, 294-4
Melt Flow 95.9 g/10 min

@Load 10.0 kg,
Temperature 360 °C
95.9 g/10 min

@Load 22.0 lb,
Temperature 680 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 154 MPa

@Load 36.5 kg,
Time 30.0 sec
22300 psi

@Load 80.5 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength, Yield 90.0 MPa
13100 psi
50mm/min; ISO 527-1/-2
Elongation at Yield 6.7 %
6.7 %
50mm/min; ISO 527-1/-2
Tensile Modulus 2.70 GPa
392 ksi
ISO 527-1/-2
Izod Impact, Notched (ISO) 6.50 kJ/m²

@Temperature 23.0 °C
3.09 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 180/A
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.650 J/cm²

@Temperature 23.0 °C
3.09 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 2700 MPa

@Strain <=0.500 %
392000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 52.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
28.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 75-1/-2
59.0 µm/m-°C

@Temperature 180 °C
32.8 µin/in-°F

@Temperature 356 °F
DIN 53752
Maximum Service Temperature, Air 180 °C
356 °F
at 50% loss of tensile strength after 20000 hr
220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1/-2
Glass Transition Temp, Tg 225 °C
437 °F
ISO 11357-1/-2
Decomposition Temperature >= 400 °C
>= 752 °F
Flammability, UL94 V-0

@Thickness 3.05 mm
V-0

@Thickness 0.120 in
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Optical Properties Metric English Comments
Refractive Index 1.63

@Thickness 1.00 mm
1.63

@Thickness 0.0394 in
ISO 489
Transmission, Visible 88 %

@Thickness 2.00 mm
88 %

@Thickness 0.0787 in
DIN 5036-3
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
ISO 60250
3.9

@Frequency 100 Hz
3.9

@Frequency 100 Hz
ISO 60250
Dielectric Strength 37.0 kV/mm
940 kV/in
IEC 60243-1
Dissipation Factor 0.00170

@Frequency 100 Hz
0.00170

@Frequency 100 Hz
IEC 60250
0.0140

@Frequency 1.00e+6 Hz
0.0140

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 100 V
100 V
Test Liquid B; IEC 60112
100 V
100 V
Test Liquid A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper throat
Zone 1 340 °C
644 °F
Feed zone
Zone 2 350 °C
662 °F
Compression
Zone 3 360 °C
680 °F
Metering-zone
Zone 4 360 °C
680 °F
Nozzle
Melt Temperature 360 °C
680 °F
Optimal
340 - 390 °C
644 - 734 °F
Injection molding/extrusion
Mold Temperature 160 °C
320 °F
Optimal
140 - 180 °C
284 - 356 °F
Injection molding
Drying Temperature 140 °C
284 °F
Dry Time 4 hour
4 hour
Descriptive Properties Value Comments
Color Light Yellow to Brownish
Commercial Status Europe
Ignition Temperature 580-600°C
DIN 54836
Primary Processing Technique Injection molding, Extrusion and Blow molding