BASF Ultrason E 6020 P PES

Category	Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer	BASF
Trade Name	Ultrason E
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultrason E 6020 P PES.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultrason E 6020 P is an unfilled, injection molding PES grade. Polyethersulfone flakes of high molecular weight and good solubility in typical solvents (N-Methylpyrrolidone, Dimethylacetamide, Dichlormethane) used e.g. in the production of membranes or coatings.

Physical Properties	Metric	English	Comments
Moisture Absorption at Equilibrium	1.0 %	1.0 %	23°C/50% R.H.; ISO 62
Viscosity Test	82 cm³/g	82 cm³/g	Viscosity number

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	90.0 MPa	13100 psi	5mm/min; ISO 527-2
Tensile Strength, Yield	90.0 MPa	13100 psi	50mm/min; ISO 527
Elongation at Break	6.7 %	6.7 %	5mm/min; ISO 527
Elongation at Yield	6.7 %	6.7 %	50mm/min; ISO 527
Tensile Modulus	2.70 GPa	392 ksi	ISO 527
Shear Modulus	0.200 GPa @Temperature 225 °C	29.0 ksi @Temperature 437 °F	ISO 6721
	0.900 GPa @Temperature 200 °C	131 ksi @Temperature 392 °F	ISO 6721
	0.950 GPa @Temperature 100 °C	138 ksi @Temperature 212 °F	ISO 6721
	1.00 GPa @Temperature 50.0 °C	145 ksi @Temperature 122 °F	ISO 6721

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	207 °C	405 °F	ISO 75-2
Glass Transition Temp, Tg	225 °C	437 °F	ISO 11357-1/-3

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	North America and Europe
Impact Modified	No
Primary Processing Technique	Injection Molding