BASF Ultrason® P 3010 MR SW 10101 PPSU

Category Polymer , Thermoplastic , Polyphenylsulfone (PPSU)
Manufacturer BASF
Trade Name Ultrason®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultrason® P 3010 MR SW 10101 PPSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Unreinforced, higher viscosity injection molding grade, flame retardant and with improved chemical resistance. This grade is black colored and demolding optimized. Abbreviated designation according to ISO 1043-1: PPSInformation provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.700 - 0.800 g/cc
0.0253 - 0.0289 lb/in³
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Water Absorption 1.2 %
1.2 %
ISO 62
Moisture Absorption at Equilibrium 0.60 %
0.60 %
23°C; 50% RH; ISO 62
Viscosity Measurement 71
71
[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage, Flow 0.0090 cm/cm
0.0090 in/in
ISO 2577, 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 2577, 294-4
Melt Flow 45.15 g/10 min

@Load 10.0 kg,
Temperature 360 °C
45.15 g/10 min

@Load 22.0 lb,
Temperature 680 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 124 MPa

@Load 36.5 kg,
Time 30.0 sec
18000 psi

@Load 80.5 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength, Yield 74.0 MPa
10700 psi
50mm/min; ISO 527-1/-2
Elongation at Yield 7.8 %
7.8 %
50mm/min; ISO 527-1/-2
Tensile Modulus 2.27 GPa
329 ksi
ISO 527-1/-2
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 2.40 J/cm²

@Temperature -30.0 °C
11.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
6.00 J/cm²

@Temperature 23.0 °C
28.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
30.6 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 75-1/-2
63.0 µm/m-°C

@Temperature 180 °C
35.0 µin/in-°F

@Temperature 356 °F
DIN 53752
Deflection Temperature at 1.8 MPa (264 psi) 196 °C
385 °F
ISO 75-1/-2
Glass Transition Temp, Tg 220 °C
428 °F
ISO 11357-1/-2
Decomposition Temperature >= 400 °C
>= 752 °F
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper throat
Zone 1 350 °C
662 °F
Feed zone
Zone 2 360 °C
680 °F
Compression
Zone 3 370 °C
698 °F
Metering-zone
Zone 4 370 °C
698 °F
Nozzle
Melt Temperature 350 - 390 °C
662 - 734 °F
Injection molding/extrusion
370 °C
698 °F
Optimal
Mold Temperature 140 - 180 °C
284 - 356 °F
Injection molding
160 °C
320 °F
Optimal
Drying Temperature 140 °C
284 °F
Dry Time 4 hour
4 hour
Descriptive Properties Value Comments
Color Black
Commercial Status Europe
Ignition Temperature 580-600°C
DIN 54836