BASF Ultrason® P 3010 PPSU Unreinforced Polyphenylsulfone

Category Polymer , Thermoplastic , Polyphenylsulfone (PPSU)
Manufacturer BASF
Trade Name Ultrason®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultrason® P 3010 PPSU Unreinforced Polyphenylsulfone.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Medium viscosity injection-molding and extrusion grade with good toughness and chemical resistance (stress crack resistance), resistant against superheated steam. The property profile makes it possible to use them in high-quality technical components and heavy-duty mass products. Conventional processing methods for thermoplastics can be applied. Ultrason® can thus be used where, for example, polyamide, polycarbonate, polyoxymethylene, and polyalkylene terephthalate are no longer suitable, primarily due to thermal or hydrolytic instability. The property spectrum of Ultrason® products allows the substitution of duromers, metals, and ceramics.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.700 - 0.800 g/cc
0.0253 - 0.0289 lb/in³
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Water Absorption <= 1.2 %
<= 1.2 %
Equilibrium; ISO 62
0.56 %

@Thickness 2.00 mm,
Time 180000 sec
0.56 %

@Thickness 0.0787 in,
Time 50.0 hour
Storage; ISO 62
1.0 %

@Thickness 2.00 mm,
Time 360000 sec
1.0 %

@Thickness 0.0787 in,
Time 100 hour
Storage; ISO 62
1.15 %

@Thickness 2.00 mm,
Time 1.08e+6 sec
1.15 %

@Thickness 0.0787 in,
Time 300 hour
Storage; ISO 62
1.2 %

@Thickness 2.00 mm,
Time 1.80e+6 sec
1.2 %

@Thickness 0.0787 in,
Time 500 hour
Storage; ISO 62
Moisture Absorption at Equilibrium 0.60 %
0.60 %
23°C; 50% RH; ISO 62
Water Vapor Transmission 100 - 150 g/m²/day
6.44 - 9.66 g/100 in²/day
DIN EN 12086
Viscosity Measurement 71
71
Viscosity number; ISO 1628
Linear Mold Shrinkage, Flow 0.0090 cm/cm
0.0090 in/in
ISO 294
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 294
Melt Flow >= 45.15 g/10 min

@Load 10.0 kg,
Temperature 360 °C
>= 45.15 g/10 min

@Load 22.0 lb,
Temperature 680 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 124 MPa

@Load 36.5 kg,
Time 30.0 sec
18000 psi

@Load 80.5 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength at Break 74.0 MPa
10700 psi
5 mm/min; ISO 527-2
Tensile Stress 30.0 MPa

@Temperature 160 °C
4350 psi

@Temperature 320 °F
35.0 MPa

@Temperature 160 °C
5080 psi

@Temperature 320 °F
40.0 MPa

@Temperature 23.0 °C
5800 psi

@Temperature 73.4 °F
60.0 MPa

@Temperature 23.0 °C
8700 psi

@Temperature 73.4 °F
70.0 MPa

@Temperature 23.0 °C
10200 psi

@Temperature 73.4 °F
Tensile Strength, Yield 74.0 MPa
10700 psi
50 mm/min; ISO 527-2
45.0 MPa

@Temperature 140 °C
6530 psi

@Temperature 284 °F
55.0 MPa

@Temperature 100 °C
7980 psi

@Temperature 212 °F
65.0 MPa

@Temperature 60.0 °C
9430 psi

@Temperature 140 °F
75.0 MPa

@Temperature 20.0 °C
10900 psi

@Temperature 68.0 °F
Elongation at Break 7.8 %
7.8 %
5mm/min; ISO 527-2
Elongation at Yield 7.8 %
7.8 %
50 mm/min; ISO 527-2
0.18 %

@Time 36000 sec,
Pressure 30.0 MPa
0.18 %

@Time 10.0 hour,
Pressure 4350 psi
ISO 899
0.20 %

@Time 3600 sec,
Pressure 6.00 MPa
0.20 %

@Time 1.00 hour,
Pressure 870 psi
180°C; ISO 899
0.28 %

@Time 36000 sec,
Pressure 42.0 MPa
0.28 %

@Time 10.0 hour,
Pressure 6090 psi
ISO 899
0.40 %

@Time 3600 sec,
Pressure 8.00 MPa
0.40 %

@Time 1.00 hour,
Pressure 1160 psi
180°C; ISO 899
0.50 %

@Pressure 6.00 MPa,
Time 360000 sec
0.50 %

@Pressure 870 psi,
Time 100 hour
180°C; ISO 899
0.50 %

@Time 3600 sec,
Pressure 10.0 MPa
0.50 %

@Time 1.00 hour,
Pressure 1450 psi
ISO 899
0.51 %

@Pressure 10.0 MPa,
Time 36000 sec
0.51 %

@Pressure 1450 psi,
Time 10.0 hour
ISO 899
0.52 %

@Pressure 10.0 MPa,
Time 360000 sec
0.52 %

@Pressure 1450 psi,
Time 100 hour
ISO 899
0.53 %

@Pressure 10.0 MPa,
Time 3.60e+6 sec
0.53 %

@Pressure 1450 psi,
Time 1000 hour
ISO 899
0.90 %

@Time 3600 sec,
Pressure 12.0 MPa
0.90 %

@Time 1.00 hour,
Pressure 1740 psi
180°C; ISO 899
1.0 %

@Time 3600 sec,
Pressure 14.0 MPa
1.0 %

@Time 1.00 hour,
Pressure 2030 psi
180°C; ISO 899
1.0 %

@Pressure 6.00 MPa,
Time 3.60e+6 sec
1.0 %

@Pressure 870 psi,
Time 1000 hour
180°C; ISO 899
1.0 %

@Pressure 8.00 MPa,
Time 360000 sec
1.0 %

@Pressure 1160 psi,
Time 100 hour
180°C; ISO 899
1.1 %

@Time 3600 sec,
Pressure 16.0 MPa
1.1 %

@Time 1.00 hour,
Pressure 2320 psi
180°C; ISO 899
1.1 %

@Time 3600 sec,
Pressure 20.0 MPa
1.1 %

@Time 1.00 hour,
Pressure 2900 psi
ISO 899
1.2 %

@Time 36000 sec,
Pressure 20.0 MPa
1.2 %

@Time 10.0 hour,
Pressure 2900 psi
ISO 899
1.25 %

@Pressure 20.0 MPa,
Time 360000 sec
1.25 %

@Pressure 2900 psi,
Time 100 hour
ISO 899
1.28 %

@Pressure 20.0 MPa,
Time 3.60e+6 sec
1.28 %

@Pressure 2900 psi,
Time 1000 hour
ISO 899
1.75 %

@Time 3600 sec,
Pressure 30.0 MPa
1.75 %

@Time 1.00 hour,
Pressure 4350 psi
ISO 899
1.9 %

@Pressure 8.00 MPa,
Time 3.60e+6 sec
1.9 %

@Pressure 1160 psi,
Time 1000 hour
180°C; ISO 899
1.9 %

@Pressure 12.0 MPa,
Time 360000 sec
1.9 %

@Pressure 1740 psi,
Time 100 hour
180°C; ISO 899
1.95 %

@Pressure 30.0 MPa,
Time 360000 sec
1.95 %

@Pressure 4350 psi,
Time 100 hour
ISO 899
2.1 %

@Pressure 30.0 MPa,
Time 3.60e+6 sec
2.1 %

@Pressure 4350 psi,
Time 1000 hour
ISO 899
2.1 %

@Pressure 14.0 MPa,
Time 360000 sec
2.1 %

@Pressure 2030 psi,
Time 100 hour
180°C; ISO 899
2.5 %

@Time 3600 sec,
Pressure 40.0 MPa
2.5 %

@Time 1.00 hour,
Pressure 5800 psi
ISO 899
2.6 %

@Time 36000 sec,
Pressure 40.0 MPa
2.6 %

@Time 10.0 hour,
Pressure 5800 psi
ISO 899
2.7 %

@Pressure 40.0 MPa,
Time 360000 sec
2.7 %

@Pressure 5800 psi,
Time 100 hour
ISO 899
2.75 %

@Time 3600 sec,
Pressure 42.0 MPa
2.75 %

@Time 1.00 hour,
Pressure 6090 psi
ISO 899
3.0 %

@Pressure 16.0 MPa,
Time 360000 sec
3.0 %

@Pressure 2320 psi,
Time 100 hour
180°C; ISO 899
3.0 %

@Pressure 40.0 MPa,
Time 3.60e+6 sec
3.0 %

@Pressure 5800 psi,
Time 1000 hour
ISO 899
3.0 %

@Pressure 42.0 MPa,
Time 360000 sec
3.0 %

@Pressure 6090 psi,
Time 100 hour
ISO 899
3.2 %

@Pressure 42.0 MPa,
Time 3.60e+6 sec
3.2 %

@Pressure 6090 psi,
Time 1000 hour
ISO 899
3.5 %

@Pressure 12.0 MPa,
Time 3.60e+6 sec
3.5 %

@Pressure 1740 psi,
Time 1000 hour
180°C; ISO 899
4.5 %

@Pressure 14.0 MPa,
Time 3.60e+6 sec
4.5 %

@Pressure 2030 psi,
Time 1000 hour
180°C; ISO 899
5.5 %

@Pressure 16.0 MPa,
Time 3.60e+6 sec
5.5 %

@Pressure 2320 psi,
Time 1000 hour
180°C; ISO 899
Creep Strength 30.0 MPa

@Time 3.60e+7 sec
4350 psi

@Time 10000 hour
in water at 95°C
33.0 MPa

@Time 3.60e+6 sec
4790 psi

@Time 1000 hour
in water at 95°C
35.0 MPa

@Time 360000 sec
5080 psi

@Time 100 hour
in water at 95°C
37.0 MPa

@Time 36000 sec
5370 psi

@Time 10.0 hour
in water at 95°C
Modulus of Elasticity 1.60 GPa

@Temperature 140 °C
232 ksi

@Temperature 284 °F
ISO 527
1.90 GPa

@Temperature 100 °C
276 ksi

@Temperature 212 °F
ISO 527
2.10 GPa

@Temperature 60.0 °C
305 ksi

@Temperature 140 °F
ISO 527
2.25 GPa

@Temperature 20.0 °C
326 ksi

@Temperature 68.0 °F
ISO 527
Tensile Modulus >= 2.27 GPa
>= 329 ksi
ISO 527-2
>= 1.60 GPa

@Temperature 140 °C
>= 232 ksi

@Temperature 284 °F
Elasticity
>= 1.90 GPa

@Temperature 100 °C
>= 276 ksi

@Temperature 212 °F
Elasticity
>= 2.10 GPa

@Temperature 60.0 °C
>= 305 ksi

@Temperature 140 °F
Elasticity
>= 2.25 GPa

@Temperature 20.0 °C
>= 326 ksi

@Temperature 68.0 °F
Elasticity
Shear Modulus 0.200 GPa

@Temperature 225 °C
29.0 ksi

@Temperature 437 °F
ISO 6721
0.700 GPa

@Temperature 200 °C
102 ksi

@Temperature 392 °F
ISO 6721
0.750 GPa

@Temperature 150 °C
109 ksi

@Temperature 302 °F
ISO 6721
0.775 GPa

@Temperature 100 °C
112 ksi

@Temperature 212 °F
ISO 6721
0.800 GPa

@Temperature 50.0 °C
116 ksi

@Temperature 122 °F
ISO 6721