BASF Ultrason® S 3010 MR UN PSU

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer BASF
Trade Name Ultrason®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultrason® S 3010 MR UN PSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Unreinforced, higher viscosity injection molding and extrusion grade, tougher, with improved chemical resistance and demolding optimized. Abbreviated designation according to ISO 1043-1: PSInformation provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.700 - 0.800 g/cc
0.0253 - 0.0289 lb/in³
Density 1.234 g/cc
0.04458 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Moisture Absorption at Equilibrium 0.30 %
0.30 %
23°C; 50% RH; ISO 62
Viscosity Measurement 72
72
[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
ISO 2577, 294-4
Linear Mold Shrinkage, Transverse 0.0073 cm/cm
0.0073 in/in
ISO 2577, 294-4
Melt Flow 55.53 g/10 min

@Load 10.0 kg,
Temperature 360 °C
55.53 g/10 min

@Load 22.0 lb,
Temperature 680 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 135 MPa

@Load 36.5 kg,
Time 30.0 sec
19600 psi

@Load 80.5 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength, Yield 75.0 MPa
10900 psi
50mm/min; ISO 527-1/-2
Elongation at Yield 5.7 %
5.7 %
50mm/min; ISO 527-1/-2
Tensile Modulus 2.60 GPa
377 ksi
ISO 527-1/-2
Izod Impact, Notched (ISO) 5.50 kJ/m²

@Temperature 23.0 °C
2.62 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 53.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
29.4 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 75-1/-2
60.0 µm/m-°C

@Temperature 180 °C
33.3 µin/in-°F

@Temperature 356 °F
DIN 53752
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
ISO 75-1/-2
Glass Transition Temp, Tg 187 °C
369 °F
ISO 11357-1/-2
Decomposition Temperature >= 400 °C
>= 752 °F
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper throat
Zone 1 330 °C
626 °F
Feed zone
Zone 2 340 °C
644 °F
Compression
Zone 3 350 °C
662 °F
Metering-zone
Zone 4 350 °C
662 °F
Nozzle
Melt Temperature 350 °C
662 °F
Optimal
330 - 390 °C
626 - 734 °F
Injection molding/extrusion
Mold Temperature 120 - 160 °C
248 - 320 °F
Injection molding
140 °C
284 °F
Optimal
Drying Temperature 140 °C
284 °F
Dry Time 4 hour
4 hour
Descriptive Properties Value Comments
Color Light Yellow to Brownish
Commercial Status Europe
Ignition Temperature 570°C
DIN 54836
Primary Processing Technique Injection molding
Copyright © lookpolymers.com All Rights Reserved