BLUESTAR PBT 6630 30% Glass Filled

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer BLUESTAR
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BLUESTAR PBT 6630 30% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT6630 is an injection molding grade, with 30% glass fiber reinforced, high heat stability, and electrical properties, easy to process. It is widely used in automotive, home appliance, E/E industry, such as connector, gear housing, and other structural parts.Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Specific Gravity 1.53 g/cc
1.53 g/cc
ISO 1183
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 250 °C
13 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 123 MPa
17800 psi
ISO 527-2/1
Elongation at Break 3.1 %
3.1 %
ISO 527-2/1
Tensile Modulus 9.01 GPa
1310 ksi
ISO 527-2/1A
Flexural Strength 189 MPa
27400 psi
ISO 178
Flexural Modulus 9.25 GPa
1340 ksi
ISO 178
Izod Impact, Notched (ISO) 7.50 kJ/m²
3.57 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 202 °C
396 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Processing Properties Metric English Comments
Nozzle Temperature 240 - 260 °C
464 - 500 °F
Melt Temperature 230 - 260 °C
446 - 500 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 120 - 140 °C
248 - 284 °F
Dry Time 3 - 4 hour
3 - 4 hour
Back Pressure 0.300 - 0.700 MPa
43.5 - 102 psi
Descriptive Properties Value Comments
Processing Screw Speed Medium-Fast