BNZ Materials Bazelite 2300 Insulating Castable

Category	Ceramic , Oxide , Aluminum Oxide
Manufacturer	BNZ Materials, Inc.
Trade Name	Bazelite
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BNZ Materials Bazelite 2300 Insulating Castable.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Blaz 2300 is a lightweight, general purpose insulating castable. Can be used for back-up or exposed to furnace conditions. Used for one-shot linings, petrochemical heaters, combustion chambers and furnace doors and covers. Frequently used in those areas that would require a 2300°F (1260°C) Insulating Fire Brick.Information provided by BNZ Materials Inc.

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/in³	Fired at 5 hrs at 816°C

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.000480 GPa @Temperature 540 °C	0.0696 ksi @Temperature 1000 °F	Fired; ASTM C268
	0.000550 GPa @Temperature 815 °C	0.0798 ksi @Temperature 1500 °F	ASTM C268
	0.000620 GPa @Temperature 1095 °C	0.0899 ksi @Temperature 2003 °F	ASTM C268
	0.000900 GPa @Temperature 104 °C	0.131 ksi @Temperature 219 °F	Dried; ASTM C268
	0.00138 GPa @Temperature 1260 °C	0.200 ksi @Temperature 2300 °F	ASTM C268
Compressive Strength	1.86 MPa @Temperature 1095 °C	270 psi @Temperature 2003 °F	Cold Crush Strength
	3.45 MPa @Temperature 815 °C	500 psi @Temperature 1500 °F	Cold Crush Strength
	3.79 MPa @Temperature 1260 °C	550 psi @Temperature 2300 °F	Cold Crush Strength
	2.21 MPa @Treatment Temp. 540 °C	320 psi @Treatment Temp. 1000 °F	Cold Crush Strength; Dried 104°C
	2.76 MPa @Treatment Temp. 104 °C	400 psi @Treatment Temp. 219 °F	Cold Crush Strength; Dried 104°C

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	1260 °C	2300 °F
Shrinkage	0.10 % @Temperature 815 °C	0.10 % @Temperature 1500 °F	Permanent Linear Change; ASTM C210
	0.20 % @Temperature 540 °C	0.20 % @Temperature 1000 °F	Permanent Linear Change; ASTM C210
	0.20 % @Temperature 1095 °C	0.20 % @Temperature 2003 °F	Permanent Linear Change; ASTM C210
	0.90 % @Temperature 1260 °C	0.90 % @Temperature 2300 °F	Permanent Linear Change; ASTM C210

Component Elements Properties	Metric	English	Comments
Al2O3	43.9 %	43.9 %
CaO	6.7 %	6.7 %
Fe2O3	3.2 %	3.2 %
MgO	0.20 %	0.20 %
Na2O	0.90 %	0.90 %	Includes K<sub>2</sub>O
SiO2	43.8 %	43.8 %
TiO2	1.8 %	1.8 %