Beijing Chemical Industry KAIFA® 2030 PET Resin

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer Beijing Chemical Industry Research Institute (Group)
Trade Name KAIFA®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Beijing Chemical Industry KAIFA® 2030 PET Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High mechanical strength, Creep resistant, Low frictionInformation provided by Beijing Chemical Industry Research Institute (Group)
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa
18100 psi
ASTM D638
Flexural Strength 190 MPa
27600 psi
ASTM D790
Charpy Impact Unnotched 8.00 J/cm²
38.1 ft-lb/in²
ISO179
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 220 °C
428 °F
ASTM D648
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 1e+6 Hz
3.0

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 21.0 kV/mm

@Thickness 2.00 mm
533 kV/in

@Thickness 0.0787 in
ASTM D149
Dissipation Factor 0.020

@Frequency 1e+6 Hz
0.020

@Frequency 1e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Processing Temperature 240 - 260 °C
464 - 500 °F
Injection Temp.
Drying Temperature 120 °C
248 °F
Dry Time 4 - 8 hour
4 - 8 hour
Injection Pressure 80.0 - 120 MPa
11600 - 17400 psi
Back Pressure 8.00 - 18.0 MPa
1160 - 2610 psi