Bhansali Engineering Abstron AP-78 EP ABS Electro Plating Applications

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade
Manufacturer Bhansali Engineering
Trade Name Abstron
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bhansali Engineering Abstron AP-78 EP ABS Electro Plating Applications.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Electroplating & Hot Stamping GradesInformation provided by Bhansali
Physical Properties Metric English Comments
Density 1.045 g/cc
0.03775 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0040 - 0.0050 cm/cm
0.0040 - 0.0050 in/in
ASTM D-955
Melt Flow 15 g/10 min

@Load 10.0 kg,
Temperature 220 °C
15 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 111
111
ASTM D-785
Tensile Strength, Yield 44.1 MPa

@Thickness 3.20 mm
6400 psi

@Thickness 0.126 in
Type 1, 5 mm/min speed; ASTM D-638
Flexural Yield Strength 64.7 MPa

@Thickness 6.40 mm
9390 psi

@Thickness 0.252 in
ASTM D-790
Flexural Modulus 2.21 GPa

@Thickness 6.40 mm
320 ksi

@Thickness 0.252 in
ASTM D-790
Izod Impact, Notched 2.451 J/cm

@Thickness 6.40 mm
4.592 ft-lb/in

@Thickness 0.252 in
ASTM D-256
3.2353 J/cm

@Thickness 3.20 mm
6.0610 ft-lb/in

@Thickness 0.126 in
ASTM D-256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 94.0 °C
201 °F
Method A - Annealed; ASTM D-648
Vicat Softening Point 106 °C
223 °F
Method B; ASTM D-1525
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
UL-94