Bhansali Engineering Abstron IMC-45V ABS-PC Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bhansali Engineering Abstron IMC-45V ABS-PC Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ABS-polycarbonate alloys for High service temperature applications.Information provided by Bhansali
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D-955
Melt Flow 9.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 9.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D-785
Tensile Strength, Yield 58.8 MPa

@Thickness 3.20 mm
 8530 psi

@Thickness 0.126 in
 Type 1; 5mm/min; ASTM D638
Flexural Yield Strength 88.3 MPa

@Thickness 6.40 mm
 12800 psi

@Thickness 0.252 in
 ASTM D790
Flexural Modulus 2.40 GPa

@Thickness 6.40 mm
 348 ksi

@Thickness 0.252 in
 ASTM D790
Izod Impact, Notched 4.90 J/cm

@Thickness 6.40 mm
 9.18 ft-lb/in

@Thickness 0.252 in
 ASTM D256
6.37 J/cm

@Thickness 3.20 mm
 11.9 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Method A - Annealed; ASTM D-648
Vicat Softening Point 130 °C
266 °F
Method B; ASTM D-1525
Flammability, UL94 HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 UL-94