Bond Laminates TEPEX® dynalite 201-C200(x)/45% Carbon – PA6.6 Consolidated Composite Laminate

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Carbon Fiber Filled
Manufacturer Bond Laminates
Trade Name TEPEX® dynalite
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bond Laminates TEPEX® dynalite 201-C200(x)/45% Carbon – PA6.6 Consolidated Composite Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Within the TEPEX® composite laminate, Polyamide 66 is a resin known for its high hardness, stiffness, abrasion resistance, heat and chemical resistances. The carbon used within this material is aerospace qualified. This material has outstanding mechanical properties and fatigue resistance.Typical application environments are structural sporting goods applications, helmet shells.Information provided by Bond Laminates, GmbH.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
Filler Content 45 %
45 %
by volume
Thickness 250 microns
9.84 mil
laminate layer thickness
Mechanical Properties Metric English Comments
Tensile Strength 725 MPa
105000 psi
transverse; ISO 527-4/5
785 MPa
114000 psi
longitudinal; ISO 527-4/5
Elongation at Break 2.1 %
2.1 %
longitudinal; ISO 527-4/5
2.1 %
2.1 %
transverse; ISO 527-4/5
Tensile Modulus 51.0 GPa
7400 ksi
transverse; ISO 527-4/5
53.0 GPa
7690 ksi
longitudinal; ISO 527-4/5
Flexural Strength 730 MPa
106000 psi
transverse; ISO 178
760 MPa
110000 psi
longitudinal; ISO 178
Flexural Modulus 44.1 GPa
6400 ksi
transverse; ISO 178
45.5 GPa
6600 ksi
longitudinal; ISO 178
Poissons Ratio 0.070
0.070
longitudinal; ISO 527-4/5
0.070
0.070
transverse; ISO 527-4/5
Charpy Impact Unnotched 11.0 J/cm²

@Temperature 23.0 °C
52.3 ft-lb/in²

@Temperature 73.4 °F
longitudinal; ISO 179/1eU
15.0 J/cm²

@Temperature -30.0 °C
71.4 ft-lb/in²

@Temperature -22.0 °F
longitudinal; ISO 179/1eU
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
DSC 3146
Maximum Service Temperature, Air 130 °C

@Time 7.20e+7 sec
266 °F

@Time 20000 hour
Relative Temperature Index; IEC 216/1
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
ISO 75-1/2
Minimum Service Temperature, Air -30.0 °C
-22.0 °F
Glass Transition Temp, Tg 70.0 °C
158 °F
DSC 3146
Processing Properties Metric English Comments
Processing Temperature 280 - 300 °C
536 - 572 °F
Descriptive Properties Value Comments
Reinforcement Area weight
200 g/m²
Fabric
twill 2/2
Fibers
carbon
Weight Rate
50% longitudinal and transverse
Yarn
3000 tex longitudinal and transverse