Borealis BorPure™ RD226CF Polypropylene Random Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer Borealis
Trade Name BorPURE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis BorPure™ RD226CF Polypropylene Random Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BorPure™ RD226CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: BorPure™ RD226CF is recommended for food packaging, lamination films, textile packaging film, and high quality stationery. Additives: BorPure™ RD226CF contains antiblock and slip agents.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.900 - 0.910 g/cc
0.0325 - 0.0329 lb/in³
base resin; ISO 1183
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Antiblock Level 1800 ppm
1800 ppm
SiO<sub>2</sub>; Borealis Method
Slip Level 1000 ppm
1000 ppm
EAA and OAA; Borealis Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 550 - 750 %
550 - 750 %
ISO 527-3
Film Elongation at Break, TD 550 - 750 %
550 - 750 %
ISO 527-3
Tensile Modulus 0.400 - 0.500 GPa
58.0 - 72.5 ksi
MD/TD; ISO 527-3
Flexural Modulus 0.800 GPa
116 ksi
ISO 178
Dart Drop, Total Energy 20.0 J

@Thickness 0.0500 mm
14.8 ft-lb

@Thickness 0.00197 in
1150N; ISO 7765-2
Coefficient of Friction 0.15 - 0.25
0.15 - 0.25
film/film; ISO 8295
Film Tensile Strength at Break, MD 30.0 - 50.0 MPa
4350 - 7250 psi
ISO 527-3
Film Tensile Strength at Break, TD 25.0 - 45.0 MPa
3630 - 6530 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 142 - 148 °C
288 - 298 °F
DSC; ISO 3146
Vicat Softening Point 130 °C

@Load 1.02 kg
266 °F

@Load 2.25 lb
A50; ISO 306
Optical Properties Metric English Comments
Haze <= 2.0 %
<= 2.0 %
ASTM D1003
Gloss >= 120 %
>= 120 %
20° of arc; ASTM D2457