Borealis BorSafe™ HE3490-LS-H HDPE Compound for Pressure Pipes
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade |
| Manufacturer | Borealis |
| Trade Name | BorSafe™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis BorSafe™ HE3490-LS-H HDPE Compound for Pressure Pipes.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BorSafe™ HE3490-LS-H is a bimodal polyethylene compound produced by the advanced Borstar® technology. It includes a combination of pigments and stabilizers to ensure excellent long-term thermal stability and UV resistance. BorSafe™ HE3490-LS-H is classified as an MRS 10.0 material (PE100). Applications: BorSafe™ HE3490-LS-H is recommended for drinking water, natural gas, pressure sewerage, relining, sea outfall, and industrial. It is especially designed for the production of larger diameter, thick wall pipe, but can be processed for the whole range of diameters.Information provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | base resin; ISO 1872-2/ISO 1183 |
| 0.959 g/cc | 0.0346 lb/in³ | compound; ISO 1872-2/ISO 1183 | |
| Environmental Stress Crack Resistance | >= 5.0 hour @Pressure 0.920 MPa, Temperature 80.0 °C |
>= 5.0 hour @Pressure 133 psi, Temperature 176 °F |
ISO 13479 |
| Oxidative Induction Time (OIT) | >= 20 min @Temperature 210 °C |
>= 20 min @Temperature 410 °F |
EN 728 |
| Carbon Black Loading | 2.0 - 2.5 % | 2.0 - 2.5 % | |
| Melt Flow | 0.25 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.25 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | >= 600 % | >= 600 % | ISO 527-2 |
| Tensile Modulus | 1.10 GPa | 160 ksi | 1mm/min; ISO 527-3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 190 - 210 °C | 374 - 410 °F | cylinder |
| Die Temperature | 200 - 210 °C | 392 - 410 °F | |
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | |
| Head Temperature | 200 - 210 °C | 392 - 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resistance To Rapid Crack Propagation (bar) | > 10 | S4 test, Pc at 0°C, test pipe 250mm, SDR11, ISO 13477 |