Borealis Borclear™ RD738CF Propylene Alpha Olefin Copolymer for Cast Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Borealis |
| Trade Name | Borclear™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis Borclear™ RD738CF Propylene Alpha Olefin Copolymer for Cast Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Borclear RD738CF is a slip and antiblock formulation propylene alpha olefin copolymer resin. It is suitable for the manufacturing of unoriented film on chill roll process.Borclear RD738CF is suitable for various high quality film applications including food packaging, high quality stationery, lamination film, textile packaging, and sealing layer in coex-structures.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in³ | ISO 1183 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 650 % | 650 % | ISO 527-3 |
| Film Elongation at Break, TD | 850 % | 850 % | ISO 527-3 |
| Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
| Secant Modulus, MD | 0.400 GPa | 58.0 ksi | ISO 527-3 |
| Secant Modulus, TD | 0.500 GPa | 72.5 ksi | ISO 527-3 |
| Impact | 59.5 | 59.5 | Damaging Force (N); ISO 7765-2 |
| Impact Test | 1.40 J | 1.03 ft-lb | Penetration Energy; ISO 7765-3 |
| Coefficient of Friction | <= 0.25 | <= 0.25 | Film/Film; ISO 8295 |
| Film Tensile Strength at Break, MD | 45.0 - 55.0 MPa | 6530 - 7980 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 35.0 - 55.0 MPa | 5080 - 7980 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 138 - 144 °C | 280 - 291 °F | ISO 3146 |
| Vicat Softening Point | 130 °C | 266 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.5 % | <= 1.5 % | ASTM D1003 |
| Gloss | >= 130 % | >= 130 % | At 20°C; ASTM D2457 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |