Borealis Bormed™ HD850MO Polypropylene Copolymer for Healthcare Applications
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | Borealis |
| Trade Name | Bormed™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis Bormed™ HD850MO Polypropylene Copolymer for Healthcare Applications.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Bormed HD850MO is a medium melt flow rate polypropylene homo polymer using the Borealis Nucleation Technology (BNT). This provides a polypropylene with excellent dimensional stability and its high crystallization temperature allows for reduced cycle time and increased output. Products made from Bormed HD850MO are characterized by excellent clarity and balanced stiffness/impact properties. Due to the high HDT-value, products made from this grade be steam-sterilized (121°C during 20 minutes).Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ISO 1183 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ISO 2039-2 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 7.5 % | 7.5 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.80 GPa | 261 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/1eA |
| Impact Test | 25.0 J @Temperature -20.0 °C |
18.4 ft-lb @Temperature -4.00 °F |
Instrumental Falling Weight - Total Penetration Energy; ISO 6603-2 |
| 35.0 J @Temperature 0.000 °C |
25.8 ft-lb @Temperature 32.0 °F |
Instrumental Falling Weight - Total Penetration Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 170 - 190 °C | 338 - 374 °F | |
| Die Temperature | 175 - 190 °C | 347 - 374 °F |