Borealis Daplen™ AK4504 TPO Compound

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polypropylene (PP) , TPO
Manufacturer Borealis
Trade Name Daplen™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ AK4504 TPO Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen AK4504 is a 30% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen AK4504 is a material with excellent impact/stiffness ratio. Thanks to its low thermal expansion this material is suitable to mold parts requiring low change of dimensions over a broad temperature range. The product is optimized to give good surface aesthetics.Daplen AK4504 is designed for acoustic applications, climate control housing, and cowl vent grillInformation provided by the Manufacturer.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
Borealis Method
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 230 °C
20 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 10.0 MPa
1450 psi
At 50 mm/min; ISO 527-2
Elongation at Break 450 %
450 %
At 50 mm/min; ISO 527-2
450 %
450 %
At 50 mm/min; ISO 527-2
Tensile Modulus 0.380 GPa
55.1 ksi
At 1 mm/min; ISO 527-2
Flexural Strength 9.30 MPa
1350 psi
ISO 178
Flexural Modulus 0.400 GPa
58.0 ksi
At 2 mm/min; ISO 178
Charpy Impact, Notched 3.50 J/cm²
16.7 ft-lb/in²
ISO 179/1eA
0.250 J/cm²

@Temperature -30.0 °C
1.19 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.300 J/cm²

@Temperature -20.0 °C
1.43 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 55.0 °C
131 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 54.0 °C
129 °F
ISO 75-2
Vicat Softening Point 75.0 °C
167 °F
B (50N); ISO 306
96.0 °C
205 °F
A (10N); ISO 306
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Polymer Mass Temp
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F