Borealis Daplen™ ED230HP Polypropylene TPO Compound

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Borealis
Trade Name Daplen™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ ED230HP Polypropylene TPO Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen™ ED230HP is a 20% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and gives a good surface quality. Applications: body panels and tailgates.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
post shrinkage (2h/90°C)
0.0080 cm/cm
0.0080 in/in
mold average
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 43.0 MPa
6240 psi
10N/132 s; ISO 2039
Tensile Strength, Yield 19.5 MPa
2830 psi
50mm/min; ISO 527-2
Elongation at Break 100 %
100 %
50mm/min; ISO 527-2
Elongation at Yield 4.5 %
4.5 %
50mm/min; ISO 527-2
Tensile Modulus 1.80 GPa
261 ksi
1mm/min; ISO 527-2
Flexural Strength 28.0 MPa
4060 psi
ISO 178
Flexural Modulus 1.90 GPa
276 ksi
2mm/min; ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature -20.0 °C
1.90 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1A
34.0 kJ/m²

@Temperature 23.0 °C
16.2 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 9.60 J/cm²
45.7 ft-lb/in²
ISO 179/1eU
NB
NB
ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.400 J/cm²

@Temperature -20.0 °C
1.90 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 52.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
28.9 µin/in-°F

@Temperature -22.0 - 176 °F
Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 56.0 °C
133 °F
ISO 75-2
Vicat Softening Point 49.0 °C

@Load 5.10 kg
120 °F

@Load 11.2 lb
ISO 306
140 °C

@Load 1.02 kg
284 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 - 260 °C
428 - 500 °F
mass temperature
Feed Temperature 40.0 - 80.0 °C
104 - 176 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Descriptive Properties Value Comments
Back Pressure low to medium
Screw Speed low to medium