Borealis Daplen™ EE040AE TPO Compound

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polypropylene (PP) , TPO
Manufacturer Borealis
Trade Name Daplen™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EE040AE TPO Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen EE040AE is an elastomer modified polypropylene compound intended for injection molding. Daplen EE040AE is a material with excellent impact /stiffness ratio. Thanks to its low thermal expansion this material is suitable to mold parts requiring low change of dimensions over a broad temperature range. This product is optimized to give good surface aesthetics.Daplen EE040AE has been developed especially for bumpers and exterior trims.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.910 g/cc
0.0329 lb/in³
ISO 1183
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Borealis Method
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 19.50 MPa
2828 psi
At 50 mm/min; ISO 527-2
Elongation at Break 570 %
570 %
At 50 mm/min; ISO 527-2
Elongation at Yield 9.0 %
9.0 %
At 50 mm/min; ISO 527-2
Tensile Modulus 1.05 GPa
152 ksi
At 1 mm/min; ISO 527-2
Flexural Strength 22.0 MPa
3190 psi
ISO 178
Flexural Modulus 1.05 GPa
152 ksi
At 2 mm/min; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 4.20 J/cm²
20.0 ft-lb/in²
ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.700 J/cm²

@Temperature -20.0 °C
3.33 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C
176 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ISO 75-2
Vicat Softening Point 63.0 °C
145 °F
B (50N); ISO 306
130 °C
266 °F
A (10N); ISO 306
Shrinkage 0.150 %

@Temperature 90.0 °C,
Time 7200 sec
0.150 %

@Temperature 194 °F,
Time 2.00 hour
Post Shrinkage; Borealis Method
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Polymer Mass Temp
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F