Borealis Daplen™ EE065AI Polypropylene Elastomer Modified

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Borealis
Trade Name Daplen™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EE065AI Polypropylene Elastomer Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen™ EE065AI is an elastomer modified polypropylene with increased crystallinity. This material has an excellent balance between impact strength and stiffness. The product is available in natural color. Applications: automotive interior parts including door panels and pockets, and center consoles.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Linear Mold Shrinkage 0.015 cm/cm
0.015 in/in
Borealis Method
Melt Flow 11.5 g/10 min

@Load 2.16 kg,
Temperature 230 °C
11.5 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 43.0 MPa
6240 psi
H 358/30; ISO 2039
Tensile Strength at Break 15.0 MPa
2180 psi
ISO 527-2
Tensile Strength, Yield 21.0 MPa
3050 psi
50mm/min; ISO 527-2
Elongation at Break 150 %
150 %
50mm/min; ISO 527-2
Elongation at Yield 5.1 %
5.1 %
50mm/min; ISO 527-2
Tensile Modulus 1.10 GPa
160 ksi
1mm/min; ISO 527-2
Flexural Strength 22.5 MPa
3260 psi
3.5% strain; ISO 178
25.0 MPa
3630 psi
ISO 178
Flexural Modulus 1.00 GPa
145 ksi
2mm/min; ISO 178
Izod Impact, Notched (ISO) 8.50 kJ/m²

@Temperature -20.0 °C
4.04 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1A
50.0 kJ/m²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO) 200 kJ/m²

@Temperature -20.0 °C
95.2 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1U
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 22.0 J/cm²

@Temperature -20.0 °C
105 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²

@Temperature -20.0 °C
4.28 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
5.50 J/cm²

@Temperature 23.0 °C
26.2 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 82.0 °C
180 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
ISO 75-2
Vicat Softening Point 56.0 °C

@Load 5.10 kg
133 °F

@Load 11.2 lb
ISO 306
143 °C

@Load 1.02 kg
289 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 - 260 °C
428 - 500 °F
mass temperature
Feed Temperature 40.0 - 80.0 °C
104 - 176 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 3.00 - 6.00 MPa
435 - 870 psi
Descriptive Properties Value Comments
Back Pressure low to medium
Emission (µgC/g) < 50
VDA 227
Fogging (mg) <2
DIN 75201
Screw Speed low to medium