Borealis Daplen™ EE108U Polypropylene TPO Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Mica Filler , Polypropylene, Mineral Reinforced
Manufacturer Borealis
Trade Name Daplen™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EE108U Polypropylene TPO Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen™ EE108U is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process. Applications: body side moldings, bumpers, and exterior trims.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.990 g/cc
0.0358 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
Borealis Method
Melt Flow 16 g/10 min

@Load 2.16 kg,
Temperature 230 °C
16 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 31.0 MPa
4500 psi
132 N/10s; ISO 2039
Tensile Strength, Yield 16.0 MPa
2320 psi
50mm/min; ISO 527-2
Elongation at Break >= 100 %
>= 100 %
50mm/min; ISO 527-2
Elongation at Yield 8.0 %
8.0 %
50mm/min; ISO 527-2
Tensile Modulus 1.00 GPa
145 ksi
1mm/min; ISO 527-2
Flexural Strength 20.0 MPa
2900 psi
ISO 178
Flexural Modulus 1.10 GPa
160 ksi
2mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -20.0 °C
2.38 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1A
37.0 kJ/m²

@Temperature 23.0 °C
17.6 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.700 J/cm²

@Temperature -20.0 °C
3.33 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
3.50 J/cm²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 61.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
33.9 µin/in-°F

@Temperature -22.0 - 176 °F
Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 51.0 °C
124 °F
ISO 75-2
Vicat Softening Point 42.0 °C

@Load 5.10 kg
108 °F

@Load 11.2 lb
ISO 306
115 °C

@Load 1.02 kg
239 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 - 260 °C
428 - 500 °F
mass temperature
Feed Temperature 40.0 - 80.0 °C
104 - 176 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Descriptive Properties Value Comments
Back Pressure low to medium
Screw Speed low to medium