Borealis Daplen™ EF341AE Polypropylene TPO Compound
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Mica Filler , Polypropylene, Mineral Reinforced |
| Manufacturer | Borealis |
| Trade Name | Daplen™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis Daplen™ EF341AE Polypropylene TPO Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Daplen™ EF341AE is a 30% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, gives a good surface quality and is easy to process. Applications: Daplen™ EF341AE has been developed especially for the car industry to be used in automotive exterior parts including fender liners, body panels, and tailgates.Information provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.145 g/cc | 0.04137 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | post shrinkage; 2 hours, 90°C |
| 0.0075 cm/cm | 0.0075 in/in | mold average;Borealis Method | |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 63.0 MPa | 9140 psi | 132 N/10s; ISO 2039 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | 20 % | 20 % | 50mm/min; ISO 178 |
| Elongation at Yield | 2.6 % | 2.6 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 3.10 GPa | 450 ksi | 1mm/min; ISO 527-2 |
| Flexural Strength | 37.0 MPa | 5370 psi | ISO 178 |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.80 kJ/m² @Temperature -20.0 °C |
1.33 ft-lb/in² @Temperature -4.00 °F |
ISO 180/1A |
| 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact Unnotched | 2.90 J/cm² @Temperature -20.0 °C |
13.8 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eU |
| 6.30 J/cm² @Temperature 23.0 °C |
30.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.240 J/cm² @Temperature -30.0 °C |
1.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.250 J/cm² @Temperature -20.0 °C |
1.19 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA | |
| 0.750 J/cm² @Temperature 23.0 °C |
3.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 54.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
30.0 µin/in-°F @Temperature -22.0 - 176 °F |
Borealis Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-2 |
| Vicat Softening Point | 64.0 °C @Load 5.10 kg |
147 °F @Load 11.2 lb |
ISO 306 |
| 150 °C @Load 1.02 kg |
302 °F @Load 2.25 lb |
ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature |
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | low to medium | |
| Screw Speed | low to medium |