Borealis Daplen™ EH104AE Polypropylene TPO Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Mica Filler , Polypropylene, Mineral Reinforced
Manufacturer Borealis
Trade Name Daplen™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EH104AE Polypropylene TPO Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen™ EH104AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, high melt flow rate and gives a good surface quality. Applications: Daplen™ EH104AE has been developed especially for the car industry to be used in automotive exterior parts including bumpers and exterior trims.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.980 g/cc
0.0354 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0015 cm/cm
0.0015 in/in
post shrinkage; 2 hours, 90°C
0.0080 cm/cm
0.0080 in/in
mold average;Borealis Method
Melt Flow 40 g/10 min

@Load 2.16 kg,
Temperature 230 °C
40 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 28.0 MPa
4060 psi
132 N/10S; ISO 2039
Tensile Strength, Yield 16.0 MPa
2320 psi
50mm/min; ISO 527-2
Elongation at Break 50 %
50 %
50mm/min; ISO 178
Elongation at Yield 5.2 %
5.2 %
50mm/min; ISO 527-2
Tensile Modulus 1.15 GPa
167 ksi
1mm/min; ISO 527-2
Flexural Strength 21.0 MPa
3050 psi
ISO 178
Flexural Modulus 1.15 GPa
167 ksi
2mm/min; ISO 178
Izod Impact, Notched (ISO) 5.50 kJ/m²

@Temperature -20.0 °C
2.62 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1A
33.0 kJ/m²

@Temperature 23.0 °C
15.7 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 3.00 J/cm²

@Temperature -20.0 °C
14.3 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.450 J/cm²

@Temperature -30.0 °C
2.14 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.550 J/cm²

@Temperature -20.0 °C
2.62 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
3.10 J/cm²

@Temperature 23.0 °C
14.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 68.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
37.8 µin/in-°F

@Temperature -22.0 - 176 °F
Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C
176 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 47.0 °C
117 °F
ISO 75-2
Vicat Softening Point 40.0 °C

@Load 5.10 kg
104 °F

@Load 11.2 lb
ISO 306
122 °C

@Load 1.02 kg
252 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 - 260 °C
428 - 500 °F
mass temperature
Feed Temperature 40.0 - 80.0 °C
104 - 176 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 3.00 - 6.00 MPa
435 - 870 psi
Descriptive Properties Value Comments
Back Pressure low to medium
Screw Speed low to medium