- Borealis Daplen™ KSR65T20 Polypropylene Compound 20% Mineral Filled
Borealis Daplen™ KSR65T20 Polypropylene Compound 20% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Borealis |
| Trade Name | Daplen™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis Daplen™ KSR65T20 Polypropylene Compound 20% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Daplen KSR65T20 is a 20% mineral filled grade for injection molding. Daplen KSR65T20 has been developed especially for the car industry, to be used in interior parts. Daplen KSR65T20 offers very good balance in stiffness/impact strength.Daplen KSR65T20 has been developed for pillar trims, door panels/pockets, and other automotive interior parts.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Borealis Method |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| 30 g/10 min @Load 5.00 kg, Temperature 230 °C |
30 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 57.0 MPa | 8270 psi | H385/30; ISO 2039 |
| Tensile Strength, Yield | 20.99 MPa | 3045 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 3.5 % | 3.5 % | At 50 mm/min; ISO 527-2 |
| Flexural Modulus | 2.10 GPa | 305 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| 5.30 J/cm² @Temperature -20.0 °C |
25.2 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179/1eA |
| 0.300 J/cm² @Temperature -20.0 °C |
1.43 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ISO 75-2 |
| Vicat Softening Point | 56.0 °C | 133 °F | B (50N); ISO 306 |
| 132 °C | 270 °F | A (10N); ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Emissions, ug C/g | 25 | VDA 277 |
| Fogging % | 97.4 | At 100°C/3 hours |
| Fogging, mg | 1 | At 100°C/ 16 hours |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® N 2875 GRN Acrylonitrile-Butadiene Rubber
- LTL Color Compounds ColorRxâ„¢ PP1-2002ARX Biocompatible Polypropylene Homopolymer
- ITW Devcon Flex Welderâ„¢ Methacrylate Adhesive FC, Off-White, Black
- Lanxess Durethan® DP 2131/20 H3.0 000000 Nylon 6, 20% Glass Fiber
- LATI Larpeek 10 K/40 PEEK, 40% Carbon Fiber Reinforced
- H.C. Starck Amperit® 235.049 Calcined Bentonite coated with Nickel-Chromium-Aluminum
- Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)
- Cosmic Plastics K43 Mineral Filled Iso Diallyl Phthalate Molding Compound
- Tra-Con Tra-Bond 724-9 Polyurethane Adhesive
- Barlog Plastics KEBAFORM C 906 LF POM Copolymer unreinforced, improved wear and friction
Copyright © lookpolymers.com All Rights Reserved