Borealis GD310U Polypropylene Compound, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Borealis |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis GD310U Polypropylene Compound, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GD310U is a 30% chemically coupled glass fiber reinforced polypropylene compound intended for injection molding. This material shows excellent mechanical properties also at elevated temperatures. Applications: GD310U has been developed especially for demanding applications in under the bonnet applications including air ducts, fans and shrouds, and lamp housings.Information provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | average process; in flow; 150x80x2mm |
| 0.0090 cm/cm | 0.0090 in/in | average process; cross flow; 150x80x2mm | |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 121 MPa | 17500 psi | 132/10s; ISO 2039 |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-2 |
| Elongation at Break | 2.8 % | 2.8 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 7.10 GPa | 1030 ksi | 1mm/min; ISO 527-2 |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 6.60 GPa | 957 ksi | 2mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -20.0 °C |
4.28 ft-lb/in² @Temperature -4.00 °F |
ISO 180/1A |
| 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact Unnotched | 4.20 J/cm² @Temperature -20.0 °C |
20.0 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eU |
| 4.80 J/cm² @Temperature 23.0 °C |
22.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.950 J/cm² @Temperature -20.0 °C |
4.52 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 0.950 J/cm² @Temperature -30.0 °C |
4.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 159 °C | 318 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ISO 75-2 |
| Vicat Softening Point | 135 °C @Load 5.10 kg |
275 °F @Load 11.2 lb |
ISO 306 |
| 164 °C @Load 1.02 kg |
327 °F @Load 2.25 lb |
ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 - 280 °C | 446 - 536 °F | mass temperature |
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | as low as possible | |
| Screw Speed | low to medium |