Borealis HD204CF Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Borealis
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis HD204CF Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HD204CF is a homopolymer film resin, suitable for the manufacturing of unoriented film on chill roll process. Applications: HD204CF is recommended for medical applications, inner layer in co extrusion, blending, textile packaging film, food packaging, lamination films, stationery folders, manufacturing of unoriented film for producers who wish to add their own slip/antiblock/antistatic additive package, and blending with formulated grades for additive adjustments. HD204CF free of slip and antiblock and without CaStearate.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.900 - 0.910 g/cc
0.0325 - 0.0329 lb/in³
base resin; ISO 1183
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 500 - 700 %
500 - 700 %
ISO 527-3
Film Elongation at Break, TD 500 - 700 %
500 - 700 %
ISO 527-3
Tensile Modulus 0.650 - 0.750 GPa
94.3 - 109 ksi
ISO 527-3
Flexural Modulus 1.35 GPa
196 ksi
5mm/min; ISO 178
Puncture Energy 14.0 J
10.3 ft-lb
1100N; ISO 7765-2
Coefficient of Friction >= 0.70
>= 0.70
film to film; ISO 8295
Film Tensile Strength at Break, MD 30.0 - 50.0 MPa
4350 - 7250 psi
ISO 527-3
Film Tensile Strength at Break, TD 25.0 - 45.0 MPa
3630 - 6530 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 162 - 166 °C
324 - 331 °F
DSC; ISO 3146
Vicat Softening Point 152 °C

@Load 5.10 kg
306 °F

@Load 11.2 lb
A50; ISO 306
Optical Properties Metric English Comments
Haze <= 2.0 %
<= 2.0 %
ASTM D1003
Gloss >= 120 %
>= 120 %
20° of arc; ASTM D2457