Borealis HK060AE Polypropylene Homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Borealis
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis HK060AE Polypropylene Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HK060AE is a special low viscosity polypropylene homopolymer compound developed to fit the production of glass matt reinforced thermoplastics. This material is also suitable as base resin for the production of PP-GF composites in the direct LFT compression and injection molding process as well as in combination with LGF concentrates on the injection molding process. Applications: HK060AE has been developed especially for applications like front end carriers, under body shieldings, noise shields, dashboard carriers, and battery supports.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Linear Mold Shrinkage 0.015 cm/cm
0.015 in/in
Borealis Method; average process
Melt Flow 125 g/10 min

@Load 2.16 kg,
Temperature 230 °C
125 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 78.0 MPa
11300 psi
132 N/10s; ISO 2039
Tensile Strength, Yield 35.0 MPa
5080 psi
50mm/min; ISO 527-2
Elongation at Break 15 %
15 %
50mm/min; ISO 527-2
Elongation at Yield 8.0 %
8.0 %
50mm/min; ISO 527-2
Tensile Modulus 1.60 GPa
232 ksi
1mm/min; ISO 527-2
Flexural Strength 45.0 MPa
6530 psi
ISO 178
Flexural Modulus 1.55 GPa
225 ksi
2mm/min; ISO 178
Izod Impact, Notched (ISO) 1.60 kJ/m²

@Temperature -20.0 °C
0.761 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1A
1.80 kJ/m²

@Temperature 23.0 °C
0.857 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 1.10 J/cm²

@Temperature -20.0 °C
5.23 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
5.50 J/cm²

@Temperature 23.0 °C
26.2 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Charpy Impact, Notched 0.0800 J/cm²

@Temperature -30.0 °C
0.381 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.0900 J/cm²

@Temperature -20.0 °C
0.428 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
0.100 J/cm²

@Temperature 23.0 °C
0.476 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
50.0 µin/in-°F

@Temperature -22.0 - 176 °F
Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 91.0 °C
196 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 54.0 °C
129 °F
ISO 75-2
Vicat Softening Point 96.0 °C

@Load 5.10 kg
205 °F

@Load 11.2 lb
ISO 306
153 °C

@Load 1.02 kg
307 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 200 - 250 °C
392 - 482 °F
mass temperature on double belt presses
220 - 270 °C
428 - 518 °F
mass temperature for direct LFT compression or injection molding
Mold Temperature 30.0 - 60.0 °C
86.0 - 140 °F
Descriptive Properties Value Comments
Injection Velocity low to medium
Users viewing this material also viewed the following: