Borealis PS65T20 Polypropylene Compound, Mineral Filled

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Borealis
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis PS65T20 Polypropylene Compound, Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PS65T20 is a 20% mineral filled polypropylene compound intended for injection and back injection molding. This material has excellent balanced mechanical properties and high melt flow rate. Applications: PS65T20 has been developed especially for the car industry to be used in automotive interior parts including trunk claddings, and other automotive interior applications.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Linear Mold Shrinkage 0.011 cm/cm
0.011 in/in
Borealis Method; average process
Melt Flow 23 g/10 min

@Load 2.16 kg,
Temperature 230 °C
23 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
88 g/10 min

@Load 5.00 kg,
Temperature 230 °C
88 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 78.0 MPa
11300 psi
358 N/30s; ISO 2039
Tensile Strength, Yield 32.0 MPa
4640 psi
50mm/min; ISO 527-2
Elongation at Yield 4.0 %
4.0 %
50mm/min; ISO 527-2
Flexural Modulus 2.80 GPa
406 ksi
2mm/min; ISO 178
Charpy Impact Unnotched 1.50 J/cm²

@Temperature -20.0 °C
7.14 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
4.50 J/cm²

@Temperature 23.0 °C
21.4 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.120 J/cm²

@Temperature -20.0 °C
0.571 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
0.250 J/cm²

@Temperature 23.0 °C
1.19 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 126 °C
259 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 64.0 °C
147 °F
ISO 75-2
Vicat Softening Point 96.0 °C

@Load 5.10 kg
205 °F

@Load 11.2 lb
ISO 306
154 °C

@Load 1.02 kg
309 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 - 260 °C
428 - 500 °F
mass temperature
Feed Temperature 40.0 - 80.0 °C
104 - 176 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Descriptive Properties Value Comments
Back Pressure low to medium
Fogging (mg) 0.6
100°C, 16h; DIN 75201
Screw Speed low to medium