Borealis SuperTR™ LE4212 Scorch Retardant, Crosslinkable Polyethylene, Water Tree Retardant Insulation for Me Power Cables

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Wire/Cable Grade
Manufacturer	Borealis
Trade Name	SuperTR™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis SuperTR™ LE4212 Scorch Retardant, Crosslinkable Polyethylene, Water Tree Retardant Insulation for Me Power Cables.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

SuperTR LE4212 is a natural, crosslinkable low density polyethylene compound, which has water tree retardant and scorch retardant properties.SuperTR LE4212 has been specifically developed as a scorch retardant, water tree retardant insulation for long life, medium voltage power cables. Because it is a Superclean material, it can be used for voltages up to 276kV.Information provided by the Manufacturer.

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in³	Base Resin; ASTM D1928/D 1505
Degree of Crosslinking	12 %	12 %	ASTM D2765

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	50	50	ASTM D2240
Tensile Strength, Yield	>= 14.3 MPa	>= 2070 psi	Heat Aging (168 hrs at 136°C); ASTM D638
	15.9 MPa	2300 psi	At 20 in/min; ASTM D638
Elongation at Break	<= 75 %	<= 75 %	Hot Creep Test (150°C,29 psi); ICEA T-28-562
	360 %	360 %	Heat Aging (168 hrs at 136°C); ASTM D412
	400 %	400 %	ASTM D638
Tensile Set	5.0 %	5.0 %	Hot Creep Test (150°C,29 psi); ICEA-T-28-562

Thermal Properties	Metric	English	Comments
Brittleness Temperature	<= -76.0 °C	<= -105 °F	ASTM D746

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Dielectric Constant	<= 2.3 @Frequency 50 Hz	<= 2.3 @Frequency 50 Hz	ASTM D150
Dielectric Strength	>= 21.7 kV/mm	>= 550 kV/in	ASTM D149
Dissipation Factor	0.00050 @Frequency 50 Hz	0.00050 @Frequency 50 Hz	ASTM D150