Borealis Xmod™ MC55T1 Polypropylene Compound 10% Mineral Filled

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer	Borealis
Trade Name	Xmod™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis Xmod™ MC55T1 Polypropylene Compound 10% Mineral Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Xmod MC55t1 is a 10% mineral filled grade based on HCPP intended for injection molding. Xmod has been developed especially for the car industry, to be used in interior parts. XMod offers very good balance in stiffness/impact strength.Xmod MC55T1 has been designed for pillar trims and other automotive interior parts.Information provided by the Manufacturer.

Physical Properties	Metric	English	Comments
Density	0.970 g/cc	0.0350 lb/in³	ISO 1183
Melt Flow	13 g/10 min @Load 2.16 kg, Temperature 230 °C	13 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
	74.2 g/10 min @Load 5.00 kg, Temperature 230 °C	74.2 g/10 min @Load 11.0 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	66.0 MPa	9570 psi	H 385/30; ISO 2039
Tensile Strength, Yield	26.3 MPa	3810 psi	At 50 mm/min; ISO 527-2
Elongation at Yield	3.3 %	3.3 %	At 50 mm/min; ISO 527-2
Tensile Modulus	2.00 GPa	290 ksi	At 1 mm/min; ISO 527-2
Flexural Modulus	2.10 GPa	305 ksi	At 2 mm/min; ISO 178
Charpy Impact Unnotched	12.0 J/cm²	57.1 ft-lb/in²	ISO 179/1eU
	6.00 J/cm² @Temperature -20.0 °C	28.6 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eU
Charpy Impact, Notched	0.690 J/cm²	3.28 ft-lb/in²	ISO 179/1eA
	0.300 J/cm² @Temperature -20.0 °C	1.43 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	114 °C	237 °F	ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi)	59.0 °C	138 °F	ISO 75-2
Vicat Softening Point	73.0 °C	163 °F	B (50N); ISO 306
	151 °C	304 °F	A (10N); ISO 306
Shrinkage	1.3 %	1.3 %	Borealis Method

Processing Properties	Metric	English	Comments
Melt Temperature	210 - 260 °C	410 - 500 °F
Mold Temperature	30.0 - 50.0 °C	86.0 - 122 °F

Descriptive Properties	Value	Comments
Emissions, ug C/g	48	VDA 277
Fogging, mg	0.2	At 100°C/ 16 hours