Braskem BS600 HDPE Blow Molding Polyethylene Copolymer

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer Braskem
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem BS600 HDPE Blow Molding Polyethylene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BS600 resin is a high-density polyethylene (HDPE), bimodal copolymer offering an outstanding combination of impact resistance and environmental stress crack resistance (ESCR). It is thus recommended for the production of containers, flasks, and bottles up to 30 liters for the transport of dangerous goods. Its other applications include bottles for agrochemicals and flasks for concentrated detergents and chemical products.
Physical Properties Metric English Comments
Density 0.954 g/cc
0.0345 lb/in³
ASTM-D792
ESCR 100% Igepal® 520 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
520 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
ESCR 10% Igepal® 198 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
198 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
Melt Flow 0.70 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.70 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ASTM-D1238
17 g/10 min

@Load 21.6 kg,
Temperature 190 °C
17 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 66
66
ASTM-D2240
Tensile Strength at Break 32.0 MPa
4640 psi
ASTM-D638
Tensile Strength, Yield 30.0 MPa
4350 psi
ASTM-D638
Flexural Modulus, 1% Secant 1030 MPa
149000 psi
ASTM-D790
Izod Impact, Notched 1.54 J/cm
2.89 ft-lb/in
ASTM-D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 71.0 °C
160 °F
ASTM-D648
Vicat Softening Point 128 °C

@Load 1.02 kg
262 °F

@Load 2.25 lb
ASTM-D1525